Polymer Property : Fatigue Strength = 400 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Fatigue Strength	400 MPa @# of Cycles 100000	58000 psi @# of Cycles 100000	R=-1, Kt=1
Materion AMC225XE T4 Aluminum/Silicon Carbide MMC Extruded Bar Aluminium alloy 2124 reinforced with 25 volume % silicon carbide particles (average size 3 micron). It is manufactured by a powder metallurgy route using high-energy mixing to ensure excellent part..
Fatigue Strength	<= 400 MPa @# of Cycles 1.00e+6	<= 58000 psi @# of Cycles 1.00e+6	after 2% elongation and heat treatment
ArcelorMittal 260 BH Bake hardening steel, Cold rolled Available in the following: uncoated (HC260B), electroglavanized (HC260B+ZE) and Extragal®/Galvannealed (HC260BD+Z)Description: The composition and processing of these steels are designed to promot..
Fatigue Strength	<= 400 MPa @# of Cycles 100000	<= 58000 psi @# of Cycles 100000
ArcelorMittal FB 450 Hot rolled ferrite-bainite steel Available in the following: uncoated (HDT450F) and Extragal® (HDT450F+Z)Description: This range of hot-rolled high strength steels has been developed to meet weight reduction requirements. It compr..
Fatigue Strength	<= 400 MPa @# of Cycles 100000	<= 58000 psi @# of Cycles 100000
ArcelorMittal HSLA 320 High strength low alloy steel for cold forming, Hot Rolled Available in the following: S315MCDescription: Steels in the HSLA (High Strength Low Alloy) range are hardened by a combination of precipitation and grain size refining, resulting in high strength w..
Fatigue Strength	<= 400 MPa @# of Cycles 2.00e+6	<= 58000 psi @# of Cycles 2.00e+6
ArcelorMittal HSLA 360 High strength low alloy steel for cold forming, Hot Rolled Available in the following: S355MCDescription: Steels in the HSLA (High Strength Low Alloy) range are hardened by a combination of precipitation and grain size refining, resulting in high strength w..
Fatigue Strength	<= 400 MPa @# of Cycles 1.00e+7	<= 58000 psi @# of Cycles 1.00e+7
ArcelorMittal HSLA 360 High strength low alloy steel for cold forming, Hot Rolled Available in the following: S355MCDescription: Steels in the HSLA (High Strength Low Alloy) range are hardened by a combination of precipitation and grain size refining, resulting in high strength w..
Fatigue Strength	400 MPa @# of Cycles 1.00e+7 , Temperature 21.0 °C	58000 psi @# of Cycles 1.00e+7 , Temperature 69.8 °F
AK Steel 410 Martensitic Stainless steel AK Steel 410 provides good corrosion resistance plus high strength and hardness. It is magnetic in both annealed and hardened conditions. A wide range of properties can be developed with different..