- Polymer Property : Modulus of Elasticity = 24500 ksi
Polymer Property : Modulus of Elasticity = 24500 ksi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Elasticity | 169 GPa @Temperature 800 °C |
24500 ksi @Temperature 1470 °F |
|
| Haynes 188 alloy, 0% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 169 GPa @Temperature 800 °C |
24500 ksi @Temperature 1470 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 169 GPa @Temperature 800 °C |
24500 ksi @Temperature 1470 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 169 GPa @Temperature 800 °C |
24500 ksi @Temperature 1470 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 169 GPa @Temperature 800 °C |
24500 ksi @Temperature 1470 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 169 GPa @Temperature 800 °C |
24500 ksi @Temperature 1470 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 169 GPa @Temperature 800 °C |
24500 ksi @Temperature 1470 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 169 GPa @Temperature 800 °C |
24500 ksi @Temperature 1470 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 169 GPa @Temperature 800 °C |
24500 ksi @Temperature 1470 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 169 GPa @Temperature 800 °C |
24500 ksi @Temperature 1470 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 169 GPa @Temperature 800 °C |
24500 ksi @Temperature 1470 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 169 GPa @Temperature 800 °C |
24500 ksi @Temperature 1470 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 169 GPa @Temperature 800 °C |
24500 ksi @Temperature 1470 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 169 GPa @Temperature 800 °C |
24500 ksi @Temperature 1470 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 169 GPa @Temperature 800 °C |
24500 ksi @Temperature 1470 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 169 GPa @Temperature 800 °C |
24500 ksi @Temperature 1470 °F |
|
| Haynes 188 alloy, hot rolled and 1175°C solution annealed plate Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 169 GPa @Temperature 800 °C |
24500 ksi @Temperature 1470 °F |
|
| Haynes 188 alloy, plate at RT after 0 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 169 GPa @Temperature 800 °C |
24500 ksi @Temperature 1470 °F |
|
| Haynes 188 alloy, plate at RT after 1000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 169 GPa @Temperature 800 °C |
24500 ksi @Temperature 1470 °F |
|
| Haynes 188 alloy, plate at RT after 16000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 169 GPa @Temperature 800 °C |
24500 ksi @Temperature 1470 °F |
|
| Haynes 188 alloy, plate at RT after 4000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 169 GPa @Temperature 800 °C |
24500 ksi @Temperature 1470 °F |
|
| Haynes 188 alloy, plate at RT after 8000 hours at 650°C (1200°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 169 GPa @Temperature 800 °C |
24500 ksi @Temperature 1470 °F |
|
| Haynes 188 alloy, plate at RT after 8000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 169 GPa | 24500 ksi | |
| Meehanite HSV Heat Resisting Cast Iron Type HSV is an iron developed essentially for engineering parts subjected to long continuous heating. It has been designed to have the maximum load bearing ability.General Meehanite information - M.. |
|||
| Modulus of Elasticity | 169 GPa @Temperature 800 °C |
24500 ksi @Temperature 1470 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 169 GPa @Temperature 800 °C |
24500 ksi @Temperature 1470 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 169 GPa @Temperature 800 °C |
24500 ksi @Temperature 1470 °F |
|
| Haynes 188 alloy, cold rolled and 1175°C solution annealed sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 169 GPa @Temperature 800 °C |
24500 ksi @Temperature 1470 °F |
|
| Haynes 188 alloy, plate at RT after 8000 hours at 760°C (1400°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 169 GPa | 24500 ksi | |
| Special Metals MONEL® 404 Copper-Nickel Alloy Data provided by California Fine Wire and the manufacturer, Special Metals. |
|||
| Modulus of Elasticity | 169 GPa | 24500 ksi | Calculated |
| Elgiloy® Co-Cr-Ni Alloy, Wire, 47% Cold Reduction (Coil Spring Range) 45-48% cold reduction is the normal coil spring range. The strength, shear modulus, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.Ge.. |
|||