Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 0.000700 GPa | 0.102 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
DuPont Performance Polymers VTR 8600 (GF-S) Peroxide Cured Fluoroelastomer (FKM)
(discontinued **) FormulationVTR-8600 |
|||
Modulus of Elasticity | 0.000700 GPa | 0.102 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
DuPont Performance Polymers GBL-200 Formulation
(discontinued **) FormulationViton® GBL-200 |
|||
Modulus of Elasticity | 0.000700 GPa | 0.102 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
DuPont Performance Polymers VTR 8655 (GBL-S) Peroxide Cured Fluoroelastomer (FKM)
(discontinued **) FormulationVTR 8655 |
|||
Modulus of Elasticity | 0.000700 GPa | 0.102 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
DuPont Performance Polymers GLT305 Peroxide Cured Fluoroelastomer (FKM) Formulation
(discontinued **) FormulationViton® GLT305 |
|||
Modulus of Elasticity | 0.000700 GPa | 0.102 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
DuPont Performance Polymers VTR 8505 Peroxide Cured Fluoroelastomer (FKM) Formulation
(discontinued **) FormulationViton® 8505 |