Polymer Property : Tensile Creep Modulus, 1 hour = 7200 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Creep Modulus, 1 hour	7200 MPa	1.04e+6 psi	ISO 899-1
Lanxess PocanÂ® T 7323 000000 PBT + PET, 20% Glass Fiber PBT+PET, 20% glass fibers, injection molding, improved surface finish, increased temperature peak load
Tensile Creep Modulus, 1 hour	7200 MPa	1.04e+6 psi	ISO 899-1
Lanxess PocanÂ® T 7323 POS151 000000 PBT + PET, 20% Glass Fiber PBT+PET, 20% glass fibers, injection molding, improved surface finish, increased temperature peak load, UV-stabilized
Tensile Creep Modulus, 1 hour	7200 MPa @Time 3600 sec	1.04e+6 psi @Time 1.00 hour	ISO 899-1
DuPont Performance Polymers Crastin® SK643FR NC010 Polybutylene Terephthalate (PBT) 20% Glass Reinforced Flame Retardant Polybutylene Terephthalate Crastin SK643FR is a flame retardant 20% glass reinforced polybutylene terephthalate molding resin. It is recognized as UL94V-0 at 0.8..
Tensile Creep Modulus, 1 hour	7200 - 16500 MPa	1.04e+6 - 2.39e+6 psi	Average value: 11700 MPa Grade Count:8
Overview of materials for PBT + PET Blend, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "PBT + PET Blend, Glass Filled". Each property range of values reported is minimum and maximum values of ..