Polymer Property : Compressive Strength = 1020 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Compressive Strength	7.00 MPa	1020 psi	1% strain over 1000 hours; ISO.899 DIN.53444
Omnia Plastica Akulon® PA 66 - Akulon 66 - at 50% RH Polyamide obtained by the polymerisation of Hexamethylenediamine and Adipic acid. It is one of the oldest engineering plastics, having been created in the USA in 1930. Due to its origin it is widely..
Compressive Strength	7.00 MPa	1020 psi	1% strain over 1000 hours; ISO.899 DIN.53444
Omnia Plastica Akulon® PA 66.6 - Akulon GX - at 50% RH Copolymer of nylon with excellent mechanical features, it combines the good impact resistances of PA6 as well as the higher stiffness of PA66. For this reason it machines very well on automatic tool..
Compressive Strength	7.00 MPa	1020 psi	1% strain over 1000 hours; ISO.899 DIN.53444
Omnia Plastica Omniamid PA6 G - G - at 50% RH Cast nylon 6. The method of production of this polyamide (i.e. the polymerisation of the caprolactam directly in the mould) allows the production of stock shapes in larger than normal dimensions, su..
Compressive Strength	7.00 MPa	1020 psi	1% strain over 1000 hours; ISO.899 DIN.53444
Omnia Plastica PVC Polyvinylchloride A widely used material, its application is under regulation in many countries for ecological reasons and it is often substituted by PP or other polymers. It is chosen for its chemical resistance.Fea..
Compressive Strength	7.00 MPa	1020 psi	0.27
Pyrotek U-1 Compressible Board U-1 is a high-temperature millboard that is easily cut, punched and shaped. It works well as a roll-cladding material and as compressible gasketing. A unique characteristic of the asbestos-free bo..
Compressive Strength	7.00 MPa	1020 psi	EN 1094-5: 1995
Skamol Group Moler SUPRA Insulating Block SKAMOL Moler insulating bricks & blocks have the following characteristics: Max. service temperature: Up to 1000Â°C (1832Â°F)Back-up insulation Excellent insulating propertiesHigh mechanical str..