Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | >= 793 MPa | >= 115000 psi | |
Niagara LaSalle StressProof® Cold Finished Steel Bar StressProof® is made by a patented process which consists of drawing the bar through a special die under heavy draft, then stress relieving it in a precisely controlled furnace. StressProof® offer.. |
|||
Tensile Strength | 793 - 1070 MPa @Thickness <=25.4 mm |
115000 - 155000 psi @Thickness <=1.00 in |
Cold Drawn Bar |
Schmolz + Bickenbach LeanDupâ„¢ 35N Stainless Steel Bar Description: LeanDupâ„¢ 35N also known as (Uranus 35 N) is a dual phase austentic-ferritic stainless steel that has the ability to become as important as 316L. It offers better corrosion resistan.. |
|||
Tensile Strength | >= 793 MPa | >= 115000 psi | 1400°F for 2 hrs and 1150°F for 4 hrs |
Schmolz + Bickenbach UGIMA® 630 Stainless Steel Bar Description: 630 UGIMA® is an improved machining martensitic precipitation hardenable grade produced only by Ugitech. It is identical in every way to standard type 630 (17-4), except with respect.. |
|||
Tensile Strength | 793 MPa | 115000 psi | As Cast |
Weartech International WT-6 Cobalt Hardfacing & Wear Resistant Alloy Applications: engine valves, pump shafts & sleeves, hot cutting & rotary knives, high pressure high temperature valves, extrusion screwsInformation provided by Weartech International |