Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | >= 1210 MPa | >= 175000 psi | ASTM D412 |
Parker Chomerics SPRING-LINE® Beryllium-Copper Gasket Description: SPRING-LINE beryllium-copper gaskets combine high levels of EMI shielding effectiveness with spring-finger wiping and low closure force properties. The high performance qualities of ber.. |
|||
Tensile Strength | 1210 MPa | 175000 psi | 40-42 HRC |
Schmolz + Bickenbach Thermodur® 2714 Extra Fine Structure - Hot Work Die Steel Description: Thermodur 2714 is an Extra Fine Structure (EFS) nickel based tool steel.Characteristics: Excellent high temperature strength; Good toughness; and Good resistance to thermal shockApplica.. |
|||
Tensile Strength | >= 1210 MPa | >= 175000 psi | |
Eagle Brass 301 Austenitic Stainless Steel, 3/4 Hardened Type 301 is a chromium-nickel stainless steel that provides high strength and good ductility with chromium and nickel contents lowered to increase the work hardening range. This permits higher tens.. |
|||
Tensile Strength | >= 1210 MPa | >= 175000 psi | |
Eagle Brass 302 Austenitic Stainless Steel, 3/4 Hardened Types 302 is a widely used variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled.Information provided by Eagle Brass Compa.. |
|||
Tensile Strength | >= 1210 MPa | >= 175000 psi | |
Eagle Brass 304L Austenitic Stainless Steel, 3/4 Hardened Type 304L is a very common variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled. Lower carbon 304L minimizes chromium ca.. |
|||
Tensile Strength | >= 1210 MPa | >= 175000 psi | |
Eagle Brass 316 Austenitic Stainless Steel, 3/4 Hardened The Mo addition increases general corrosion resistance to pitting from chloride ion solutions, and provides increased strength at elevated temperatures. Properties are similar to those of Type 304 .. |
|||
Tensile Strength | >= 1210 MPa | >= 175000 psi | |
Eagle Brass 316L Austenitic Stainless Steel, 3/4 Hardened Type 316L is an extra-low carbon version of Type 316 that minimizes carbide precipitation. Typical uses include exhaust manifolds, furnace parts, heat exchangers, jet engine parts, pharmaceutical a.. |
|||
Tensile Strength | >= 1210 MPa | >= 175000 psi | |
Eagle Brass 304 Austenitic Stainless Steel, 3/4 Hardened Types 304 is a widely used variation of the basic 18-8 grade with variations of nickel, chromium and carbon content. It is weakly magnetic when cold rolled.Information provided by Eagle Brass Compa.. |