Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 56 g/10 min @Load 5.00 kg, Temperature 190 °C |
56 g/10 min @Load 11.0 lb, Temperature 374 °F |
|
Total Finaprene® 435 Styrene-Butadiene TPE Copolymer Compounded to 56 MFI
(discontinued **) Styrene-Butadiene CopolymerDescription: Finaprene® is a thermoplastic elastomer type radial styrene-butadiene block copolymer. Thanks to its medium molecular weight, Finaprene® 435 provides excel.. |
|||
Melt Flow | 56 g/10 min @Load 5.00 kg, Temperature 260 °C |
56 g/10 min @Load 11.0 lb, Temperature 500 °F |
Estimated using room temperature density; ISO 1133 |
Lanxess Pocan® KU 1-7625 901510 PBT + PC, 20% Glass Fiber PBT+PC, 20% glass fibers, injection molding, low tendency to warp, improved surface finish |
|||
Melt Flow | 56 g/10 min @Load 2.16 kg, Temperature 235 °C |
56 g/10 min @Load 4.76 lb, Temperature 455 °F |
|
Arkema Group Rilsan® BMF Nylon 11 (Dry) Designation ISO 1874-PA11,M,12-010Rigid grade for injection molding. Available color: natural. Additive free.Good melt viscosity. Outstanding ability to mold part with high length-thickness ratio an.. |
|||
Melt Flow | 56 g/10 min @Load 2.16 kg, Temperature 235 °C |
56 g/10 min @Load 4.76 lb, Temperature 455 °F |
|
Arkema Group Rilsan® BMF Nylon 11 (Conditioned) Designation ISO 1874-PA11,M,12-010Rigid grade for injection molding. Available color: natural. Additive free.Good melt viscosity. Outstanding ability to mold part with high length-thickness ratio an.. |