Polymer Property : Melt Flow = 41 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Flow	41 g/10 min @Load 5.00 kg, Temperature 260 Â°C	41 g/10 min @Load 11.0 lb, Temperature 500 Â°F	Estimated using room temperature density; ISO 1133
Lanxess DurethanÂ® BG 30 X 000000 Nylon 6, 30% Glass Fiber PA 6, injection molding grade, 30% glass fibers/glass spheres, good surface, low warpage
Melt Flow	41 g/10 min @Load 2.16 kg, Temperature 250 Â°C	41 g/10 min @Load 4.76 lb, Temperature 482 Â°F	Calculated from MVR using melt density; ISO 1133
Lanxess PocanÂ® B 7375 000000 PBT, White Pigment PBT, 25% white pigments, injection molding, improved light reflection, low tendency to warp
Melt Flow	41 g/10 min @Load 2.16 kg, Temperature 270 Â°C	41 g/10 min @Load 4.76 lb, Temperature 518 Â°F	Estimated using room temperature density; ISO 1133
Lanxess PocanÂ® KU 2-7205 000000 PBT PBT, non-reinforced, injection molding, extrusion, flame retardant
Melt Flow	41 g/10 min @Load 5.00 kg, Temperature 270 Â°C	41 g/10 min @Load 11.0 lb, Temperature 518 Â°F	Calculated from MVR using melt density; ISO 1133
Lanxess PocanÂ® S 7926 000000 PBT PBT, non-reinforced, injection molding, extrusion, flame retardant, impact modified
Melt Flow	41 g/10 min	41 g/10 min	ASTM D1238
ExxonMobil Escorene™ UL 04028CC Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: UL 04028CC is a copolymer of ethylene and vinyl acetate.Availability: Africa & Middle East and Europe Additive: Antiblock: NoSlip: No Thermal Stabilizer: Yes Applications: Hot..
Melt Flow	41 g/10 min @Load 2.16 kg, Temperature 230 °C	41 g/10 min @Load 4.76 lb, Temperature 446 °F	cm<sup>3</sup>/10min Melt Volume-flow Rate; ISO 1133
DSM Arnitel® EL250 TPC-ET Injection Molding