Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 21.6 g/10 min @Load 10.0 kg, Temperature 380 °C |
21.6 g/10 min @Load 22.0 lb, Temperature 716 °F |
|
Lehmann & Voss LUVOCOM® 1105-7786 PEEK, with PTFE Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Emergency running property.Improved wear behaviour, low warpage.High chemical resistance p.. |
|||
Melt Flow | 21.6 g/10 min @Load 5.00 kg, Temperature 380 °C |
21.6 g/10 min @Load 11.0 lb, Temperature 716 °F |
|
Lehmann & Voss LUVOCOM® 1105-8350 PEEK, with carbon fiber, PTFE, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts; low thermal coefficient of expansion.Dynamic stressed parts at high m.. |
|||
Melt Flow | 21.6 g/10 min @Load 1.20 kg, Temperature 300 °C |
21.6 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
Teijin Panlite® L-1225L Standard (mold release/ice color grade) Polycarbonate Resin Thin-wall injection moldings grade of high fluidity. It has an improved mold release property and is bluish-tinted to exhibit clear color.Applications:Comparatively large-size components of mechanic.. |
|||
Melt Flow | 21.6 g/10 min @Load 1.20 kg, Temperature 300 °C |
21.6 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
Teijin Panlite® LV-2225L Standard (mold release/ice color grade) Polycarbonate Resin Flame retardant and mold release grade with high fluidity, while maintaining intrinsic transparency of polycarbonate resin. It is suitable for thin wall injection moldings.Applications:Electric, ele.. |