Polymer Property : Melt Flow = 2.25 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Flow	2.25 g/10 min	2.25 g/10 min	Cond. Q; ASTM D1238
Multibase Nylex™ 2185 R15 Polyamide + PP Glass fiber reinforcement, 15% Filler by Weight. Features: Crack Resistance, GoodDimensional Stability, GoodImpact Resistance, GoodMoisture ResistantProcessability, GoodForms:PelletsProcessing Metho..
Melt Flow	2.25 g/10 min @Load 2.16 kg, Temperature 230 °C	2.25 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
Multibase Multi-Pro® 5002 CU Natural Polypropylene Forms:PelletsProcessing Methods:Injection MoldingFeatures:Gloss, LowInformation provided by Multibase
Melt Flow	2.25 g/10 min @Load 2.16 kg, Temperature 190 °C	2.25 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Eastman 1840A Polyethylene (discontinued **) Polyethylene 1840A is a low-density formulation with no slip or antiblock. It is suggested for injection molding applications requiring good stiffness, gloss, good processability or layflat properti..
Melt Flow	2.25 g/10 min @Load 2.16 kg, Temperature 190 °C	2.25 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Eastman 1840E Polyethylene (discontinued **) Polyethylene 1840E is a low-density formulation for general extrusion.Eastman Chemical Company sold its polyethylene business to Westlake Chemical Corporation in Dec. 2006. This grade no longer app..
Melt Flow	2.25 g/10 min @Load 2.16 kg, Temperature 230 Â°C	2.25 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ASTM D1238
Ineos H02C-00 Polypropylene Homopolymer This is a low flow rate, high clarity homopolymer designed for extrusion, thermoforming, blow molding, and rigid packaging. Applications that require good see-through clarity combined with good hea..
Melt Flow	2.25 g/10 min	2.25 g/10 min	ExxonMobil Method
ExxonMobil LD 419.MV Wire & Cable Resin (discontinued **) LD 419.MV is a LDPE designed for wire and cable applications and is suitable for making crosslinkable compounds for medium voltage insulation.Information provided by ExxonMobil Chemical