Polymer Property : Melt Flow = 0.14 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Flow	0.14 g/10 min @Load 2.16 kg, Temperature 190 °C	0.14 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
NOVA Chemicals Novapol® HD-2100-U MDPE Extrusion Resin Features: Excellent ESCR and toughness, high strength, excellent processability.Applications: pipe, water pipe, fuel gas pipe, re-lining pipe, steel pipe coating.Data provided by the manufacturer.
Melt Flow	0.14 g/10 min @Load 2.16 kg, Temperature 190 °C	0.14 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
NOVA Chemicals Novapol® HD-2100-A MDPE Extrusion Resin (discontinued **) Features: Excellent ESCR and toughness, high strength, excellent processability.Applications: pipe, water pipe, fuel gas pipe, re-lining pipe, steel pipe coating.Data provided by the manufacturer.
Melt Flow	0.14 - 0.22 g/10 min @Load 2.16 kg, Temperature 190 Â°C	0.14 - 0.22 g/10 min @Load 4.76 lb, Temperature 374 Â°F	ASTM D1238
LG Chemical SEETEC PB283 HDPE Features: This high molecular weight, hexane copolymer is tailored for light-weight blow-molded containers that require: Good stiffness and Excellent processabilityAdditives: Anti-OxidantsApplicatio..
Melt Flow	0.14 g/10 min @Load 2.16 kg, Temperature 190 °C	0.14 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM-D1238
Braskem TU3001 LDPE Blown Film Extrusion Polyethylene TU3001 is a low-density polyethylene (LDPE) with high molecular weight, excellent mechanical properties, and good processability. These qualities ensure the production of films with uniform thicknes..
Melt Flow	0.14 g/10 min @Load 2.16 kg, Temperature 190 °C	0.14 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM-D1238
Braskem TX7001 LDPE Blown Film Extrusion Polyethylene TX7001 is a low-density polyethylene (LDPE) with high molecular weight designed to satisfy those applications that require high mechanical strength and environmental stress cracking resistance (ESCR..