Physical Properties | Metric | English | Comments |
---|---|---|---|
Linear Mold Shrinkage, Flow | 0.00200 cm/cm @Thickness 3.17 mm |
0.00200 in/in @Thickness 0.125 in |
ASTM D955 |
Oxford Polymers Oxnilon 6-60GF(DRY) PA6, 60% Glass Fiber Reinforced, Dry Product Description: Glass Fiber (60% Reinforced), Nylon 6 injection molding grade Processing and Delivery Form: Pellets and Injection MoldingAdditives: Release Agents, Lubricants and Heat Stabiliz.. |
|||
Linear Mold Shrinkage, Flow | 0.00200 cm/cm @Thickness 3.17 mm |
0.00200 in/in @Thickness 0.125 in |
ASTM D955 |
Oxford Polymers PC 30CF-925 Black PC, 30% Carbon Fiber Reinforced Product Description: Glass Fiber (30% Reinforced), PBT injection molding grade Processing and Delivery Form: Pellets and Injection MoldingAdditives: Release Agents Special Characteristics: High Str.. |
|||
Linear Mold Shrinkage, Flow | 0.00200 cm/cm @Thickness 3.17 mm |
0.00200 in/in @Thickness 0.125 in |
ASTM D955 |
Oxford Polymers PEEK-20CF-Black PEEK, 20% Carbon Fiber Reinforced Product Description: Carbon Fiber (20% Reinforced), PEEK, Polyetheretherketone, injection molding grade Processing and Delivery Form: Pellets and Injection MoldingAdditives: Carbon fiber Special Ch.. |
|||
Linear Mold Shrinkage, Flow | 0.00200 cm/cm @Thickness 3.17 mm |
0.00200 in/in @Thickness 0.125 in |
ASTM D955 |
Oxford Polymers PPS-30GF-10PTFE-BK PPS, 30% Glass Fiber Reinforced, 10% PTFE Product Description: Glass Fiber (30% Reinforced), 10% PTFE, Polyphenylene sulfide injection molding grade Processing and Delivery Form: Pellets and Injection MoldingAppearance: BlackInformation pr.. |
|||
Linear Mold Shrinkage, Flow | 0.00200 - 0.00450 cm/cm | 0.00200 - 0.00450 in/in | Injection; ISO 2577 |
Raschig Group 6502 DAIP Diallyl Phthalate (DAP), Cast, Mineral Filler Glass-fiber reinforced diallyl isophthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensi.. |
|||
Linear Mold Shrinkage, Flow | 0.00200 - 0.00400 cm/cm | 0.00200 - 0.00400 in/in | Injection and Compression; ISO 2577 |
Raschig Group DECAL® 666/8/2B Phenolic Glass-fiber reinforced phenolic molding compound. Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and mechanical properties. This product meets the allowe.. |
|||
Linear Mold Shrinkage, Flow | 0.00200 - 0.00400 cm/cm | 0.00200 - 0.00400 in/in | ISO 2577 |
Raschig Group EN 5004 Epoxy Molding Compound Mica reinforced molding compound. Low mold shrinkage and post-shrinkage, very good electrical values, outstanding heat resistance, very goo pourablity. This product meets the allowed upper limits fo.. |
|||
Linear Mold Shrinkage, Flow | 0.00200 - 0.00500 cm/cm | 0.00200 - 0.00500 in/in | Injection; ISO 2577 |
Raschig Group RALUPOL® 4802 UP Polyester Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, good electrical values, excellent heat resistance, outstanding pourability. This product meets the allowed u.. |
|||
Linear Mold Shrinkage, Flow | 0.00200 - 0.00500 cm/cm | 0.00200 - 0.00500 in/in | Injection; ISO 2577 |
Raschig Group RALUPOL® 802 UP Polyester Glass-fiber reinforced polyester molding compound. Low molding shrinkage and post-shrinkage, good electrical values, good mechanical strength, good heat resistance. This product meets the allowed up.. |
|||
Linear Mold Shrinkage, Flow | 0.00200 - 0.00500 cm/cm | 0.00200 - 0.00500 in/in | Injection; ISO 2577 |
Raschig Group RALUPOL® 804 UP Polyester Glass-fiber reinforced polyester molding compound. Low molding shrinkage and post-shrinkage, good electrical values, good mechanical strength. This product meets the allowed upper limits for heavy m.. |