Physical Properties | Metric | English | Comments |
---|---|---|---|
Particle Size | 31 µm | 31 µm | Average Diameter |
Potters Industries Conduct-O-Fil® SN325P25-ALT1 Silver-coated Nickel Granules Applications:EMI shieldingConductive adhesivesZ-axis conductive filmsAdvantages:Stable at high temperaturesParticles can be magnetically alignedLow density version (LD) has 10% less mass per volumeI.. |
|||
Particle Size | 31 - 37 µm | 31 - 37 µm | 50% |
H.C. Starck Amperit® 105.074 Agglomerated Sintered Molybdenum (Mo) |
|||
Particle Size | 31 - 38 µm | 31 - 38 µm | 50% |
H.C. Starck Amperit® 110.2 Agglomerated Sintered (Mo-Mo2C) |
|||
Particle Size | 31 - 37 µm | 31 - 37 µm | 50% |
H.C. Starck Amperit® 583.054 Chromium Carbide-Nickel 83-17 (Cr3C2-Ni) |
|||
Particle Size | 31 - 39 µm | 31 - 39 µm | 50% |
H.C. Starck Amperit® 588.074 Chromium Carbide-Nickel Chromium 75-25 (Cr3C2-NiCr) 45/15 µm |
|||
Particle Size | 31 µm | 31 µm | Minimum of 90% less than |
H.C. Starck Amperit® 704 Chromium Oxide (Cr2O3) 99.5% |
|||
Particle Size | 31 µm | 31 µm | Minimum of 85% less than |
H.C. Starck Amperit® 704.053 Chromium Oxide (Cr2O3) 99.5% |
|||
Particle Size | 31 µm | 31 µm | Minimum of 90% less than |
H.C. Starck Amperit® 740 Aluminum Oxide (Al2O3) |
|||
Particle Size | 31 µm | 31 µm | Minimum of 95% less than |
H.C. Starck Amperit® 740.8 Aluminum Oxide (Al2O3) |
|||
Particle Size | 31 µm | 31 µm | Minimum of 90% less than |
H.C. Starck Amperit® 744 Aluminum Oxide-Titanium Oxide 87-13 (Al2O3 - TiO2) |
|||
Particle Size | 31 µm | 31 µm | Minimum of 95% less than |
H.C. Starck Amperit® 745.8 Aluminum Oxide-Titanium Oxide 60-40 (Al2O3-TiO2) |
|||
Particle Size | 31 µm | 31 µm | Minimum of 90% less than |
H.C. Starck Amperit® 750 Aluminum Oxide-Zirconium Oxide 60-40 (Al2O3-ZrO2) |
|||
Particle Size | 31 µm | 31 µm | Minimum of 90% less than |
H.C. Starck Amperit® 825 Zirconium Oxide-Yttrium Oxide 93-7 (ZrO2-Y2O3) |
|||
Particle Size | 31 - 39 µm | 31 - 39 µm | 50% |
H.C. Starck Amperit® 827.054 Zirconium Oxide-Yttrium Oxide 93-7 (ZrO2-Y2O3) |
|||
Particle Size | 31 - 37 µm | 31 - 37 µm | MV |
H.C. Starck Amperit® 552.074 Tungsten Carbide - Chromium Carbide-Nickel 73-20-7 (WC-CrC-Ni) |
|||
Particle Size | 31 - 38 µm | 31 - 38 µm | 50% |
H.C. Starck Amperit® 599.074 Agglomerated Sintered Molybdenum Carbide (Cr2O3) |
|||
Particle Size | 31 µm | 31 µm | Minimum of 85% less than |
H.C. Starck Amperit® 703.053 Chromium Oxide (Cr2O3) 99.5% |
|||
Particle Size | 31 µm | 31 µm | Minimum of 85% less than |
H.C. Starck Ampersint® AISI 316 L 31 µm For P/M, HIP/CIP, MIM AISI 316 L is a type of low carbon austenitic Cr-Ni-Mo stainless steel with good oxidation resistance in intermittent service to 870°C and in continuous service to 925°C, resistance to intercr.. |
|||
Particle Size | 31 µm | 31 µm | |
Silberline Aquasil® "BP" 3641 Silberline has specifically created Aquasil® BP grades for aqueous architectural and industrial maintenance coatings. This family offers a cost-effective alternative for achieving stability and .. |
|||
Particle Size | 31 µm | 31 µm | |
Silberline SilBerCote® 3641-10Z SilBerCote® Z polymer treated aluminum pigments are resistant to acid and alkali staining, while providing enhanced electrical charge resistance in finished coatings. Product is typically formula.. |
|||
Particle Size | 31 µm | 31 µm | |
Silberline SilBerCote® PC 4352Z SilBerCote® PC Z can be formulated into post-blend and bonded metallic powder coatings. The organic surface treatment on the flake imparts improved chemical and environmental resistance propertie.. |
|||
Particle Size | 31 µm | 31 µm | |
Silberline Sparkle Silver® 3641 Sparkle Silver® 3641 is a coarse, regular purity, non-leafing aluminum pigment. It is characterized by high sparkle, a white face color and deep flop. An acid resistant purity version, Sparkle Si.. |
|||
Particle Size | 31 µm | 31 µm | Average Diameter |
Potters Industries Conduct-O-Fil® SN40P18 Silver-coated Nickel Granules Applications:EMI shieldingConductive adhesivesZ-axis conductive filmsAdvantages:Stable at high temperaturesParticles can be magnetically alignedLow density version (LD) has 10% less mass per volumeI.. |
|||
Particle Size | 31 - 39 µm | 31 - 39 µm | 50% |
H.C. Starck Amperit® 529.074 Tungsten Carbide - Hastalloy C 85-15 (NiMoCrFeCo) |
|||
Particle Size | 31 - 39 µm | 31 - 39 µm | 50% |
H.C. Starck Amperit® 584.054 Chromium Carbide-Nickel Chromium 75-25 (Cr3C2-NiCr) |