Polymer Property : Linear Mold Shrinkage, Transverse = 0.026 in/in Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage, Transverse	0.026 cm/cm @Time 86400 sec	0.026 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP RL002 PA 66 LNP LUBRICOMP* RL002 is a compound based on Nylon 66 resin containing 10% PTFE. Added features of this material include: Wear Resistant.
Linear Mold Shrinkage, Transverse	0.026 cm/cm @Time 86400 sec	0.026 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRILOY R2000A PA 66 LNP LUBRILOY* R2000A is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Transverse	0.026 cm/cm @Time 86400 sec	0.026 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRILOY R2000A PA 66 LNP LUBRILOY* R2000A is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Transverse	0.026 cm/cm @Time 86400 sec	0.026 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRILOY R2000A PA 66 (Asia Pacific) LNP LUBRILOY* R2000A is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.026 cm/cm @Time 86400 sec	0.026 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRILOY R2000A PA 66 (Asia Pacific) LNP LUBRILOY* R2000A is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.026 cm/cm @Time 86400 sec	0.026 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRILOY R2000A PA 66 (Europe-Africa-Middle East) LNP LUBRILOY* R2000A is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.026 cm/cm @Time 86400 sec	0.026 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRILOY R2000A PA 66 (Europe-Africa-Middle East) LNP LUBRILOY* R2000A is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.026 cm/cm @Time 86400 sec	0.026 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP KZ001L Acetal Copoly LNP* THERMOCOMP* KZ001L is a compound based on Acetal Copolymer resin containing 5% Milled Glass. Added features of this material include: Low Extractible.
Linear Mold Shrinkage, Transverse	0.026 cm/cm @Time 86400 sec	0.026 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP KZ001L Acetal Copoly (Asia Pacific) LNP* Thermocomp* KZ001L is a compound based on Acetal Copolymer resin containing Glass Fiber. Added features of this material include: Low Extractible.
Linear Mold Shrinkage, Transverse	0.026 cm/cm @Time 86400 sec	0.026 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP V1000SU PA LNP* Thermotuf* V1000SU is a compound based on Nylon resin. Added features of this material include: Heat Stabilized, UV Stabilized.
Linear Mold Shrinkage, Transverse	0.026 cm/cm @Time 86400 sec	0.026 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP V1000UXC PA LNP* Thermotuf* V1000UXC is a compound based on Nylon resin. Added features of this material include: UV Stabilized.
Linear Mold Shrinkage, Transverse	0.026 cm/cm @Time 86400 sec	0.026 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOTUF V1000SU PA LNP* Thermotuf* V1000SU is a compound based on Nylon resin. Added features of this material include: Heat Stabilized, UV Stabilized.
Linear Mold Shrinkage, Transverse	0.026 cm/cm @Time 86400 sec	0.026 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP Thermotuf V1000SU PA LNP* Thermotuf* V1000SU is a compound based on Nylon resin. Added features of this material include: Heat Stabilized, UV Stabilized.This data was supplied by SABIC-IP for the Americas region.
Linear Mold Shrinkage, Transverse	0.026 cm/cm @Time 86400 sec	0.026 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOTUF V1000SU PA (Asia Pacific) LNP* Thermotuf* V1000SU is a compound based on Nylon resin. Added features of this material include: Heat Stabilized, UV Stabilized.