Polymer Property : Linear Mold Shrinkage, Transverse = 0.0134 in/in Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage, Transverse	0.0134 cm/cm @Time 86400 sec	0.0134 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP KFL32R Acetal Copolymer LNP LUBRICOMP* KFL32R is a compound based on Acetal Copolymer resin containing 10% Glass Fiber, 15% PTFE. Added feature of this material is: Easy Release, Wear Resistant.
Linear Mold Shrinkage, Transverse	0.0134 cm/cm @Time 86400 sec	0.0134 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP RFN16S PA 66 LNP LUBRICOMP* RFN16S is a compound based on Nylon 66 resin containing 30% Glass Fiber, 5% MOS2. Added features of this material include: Heat Stabilized, Wear Resistant.
Linear Mold Shrinkage, Transverse	0.0134 cm/cm @Time 86400 sec	0.0134 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP RFN16SXZ PA 66 LNP LUBRICOMP* RFN16SXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber, 5% MOS2. Added features of this material include: Heat Stabilized, Wear Resistant.
Linear Mold Shrinkage, Transverse	0.0134 cm/cm @Time 86400 sec	0.0134 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP RF008XXZ PA 66 LNP THERMOCOMP* RF008XXZ is a compound based on Nylon 66 resin containing 40% Glass Fiber.
Linear Mold Shrinkage, Transverse	0.0134 cm/cm @Time 86400 sec	0.0134 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP WF006L PBT LNP* THERMOCOMP* WF006L is a compound based on PBT resin containing 30% Glass Fiber. Added feature of this material is: Low Extractible.