Polymer Property : Linear Mold Shrinkage, Transverse = 0.0115 in/in Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage, Transverse	0.0115 cm/cm @Time 86400 sec	0.0115 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP RFL36XXY PA 66 LNP* LUBRICOMP* RFL36XXY is a compound based on Nylon 66 containing 30% Glass Fiber, 15% PTFE. Added feature of this grade is: Wear Resistant.
Linear Mold Shrinkage, Transverse	0.0115 cm/cm @Time 86400 sec	0.0115 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Lubriloy Z2000 PPE+PS LNP* Lubriloy* Z2000 is a compound based on PPE+PS Blend resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP fo..
Linear Mold Shrinkage, Transverse	0.0115 cm/cm @Time 86400 sec	0.0115 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP Lubriloy Z2000 PPE+PS LNP* Lubriloy* Z2000 is a compound based on PPE+PS Blend resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP fo..
Linear Mold Shrinkage, Transverse	0.0115 cm/cm @Time 86400 sec	0.0115 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRILOY Z2000 PPE+PS (Asia Pacific) LNP* Lubriloy* Z2000 is a compound based on PPE+PS Blend resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.0115 cm/cm @Time 86400 sec	0.0115 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRILOY Z2000 PPE+PS (Asia Pacific) LNP* Lubriloy* Z2000 is a compound based on PPE+PS Blend resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.0115 cm/cm @Time 86400 sec	0.0115 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRILOY Z2000 PPO LNP* LUBRILOY* Z2000 is a compound based on PPO resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Transverse	0.0115 cm/cm @Time 86400 sec	0.0115 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRILOY Z2000 PPO LNP* LUBRILOY* Z2000 is a compound based on PPO resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Transverse	0.0115 cm/cm @Time 86400 sec	0.0115 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP STAT-KON PFD06 PA 6 LNP* STAT-KON* PFD06 is a compound based on Nylon 6 resin containing 30% Glass Fiber. Added features of this material include: Electrically Conductive.
Linear Mold Shrinkage, Transverse	0.0115 cm/cm @Time 86400 sec	0.0115 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP STAT-KON PFD06 PA 6 (Asia Pacific) LNP* Stat-kon* PFD06 is a compound based on Nylon 6 resin containing Glass Fiber, Carbon Powder. Added features of this material include: Electrically Conductive.
Linear Mold Shrinkage, Transverse	0.0115 cm/cm @Time 86400 sec	0.0115 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP MB006S PP LNP THERMOCOMP* MB006S is a compound based on Polypropylene resin containing 30% Glass Bead. Added features of this material include: Heat Stabilized.