Zylog Neoplast® 243 HOFR Thermoplastic Vulcanizate

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Vulcanizate Elastomer (TPV)
Manufacturer Zylog Plastalloys
Trade Name Neoplast®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Zylog Neoplast® 243 HOFR Thermoplastic Vulcanizate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Neoplast 243 HOFR is a flame retardant thermoplastic vulcanizate (TPV) compound, based on polyolefin chemistry, suitable for Injection Molding and Extrusion applications.RoHS Compliant, UV StabilizedInformation provided by Zylog Plastalloys Pvt. Ltd.
Physical Properties Metric English Comments
Specific Gravity 1.10 g/cc
1.10 g/cc
ASTM D 792
Mechanical Properties Metric English Comments
Hardness, Shore D 43
43
ASTM D 2240
45

@Treatment Temp. 150 °C,
Time 605000 sec
45

@Treatment Temp. 302 °F,
Time 168 hour
Heat Aging; ASTM D 2240/ASTM D573
Tensile Strength, Ultimate 16.7 MPa
2420 psi
500 mm/min; ASTM D 412
20.8 MPa

@Treatment Temp. 150 °C,
Time 605000 sec
3020 psi

@Treatment Temp. 302 °F,
Time 168 hour
Heat Aging; ASTM D 412/ASTM D 573
Elongation at Break 600 %
600 %
500 mm/min; ASTM D 412
450 %

@Treatment Temp. 150 °C,
Time 605000 sec
450 %

@Treatment Temp. 302 °F,
Time 168 hour
Heat Aging; ASTM D 412/ASTM D 573
100% Modulus 0.0108 GPa
1.56 ksi
500 mm/min; ASTM D 412
Tear Strength 79.4 kN/m
454 pli
500 mm/min; ASTM D 624
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 140 °C
284 °F
Continuous; SAE J 2236
Brittleness Temperature -50.0 °C
-58.0 °F
ASTM D 746
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
Oxygen Index 26 %
26 %
ASTM D 2863
Electrical Properties Metric English Comments
Volume Resistivity 6.90e+16 ohm-cm
6.90e+16 ohm-cm
ASTM D 257
Dielectric Constant 2.5
2.5
ASTM D 150
Dielectric Strength 31.0 kV/mm
787 kV/in
ASTM D 149