Westlake Plastics Propylux® 290 Polypropylene, Heat Stabilized

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	Westlake Plastics
Trade Name	Propylux®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Westlake Plastics Propylux® 290 Polypropylene, Heat Stabilized.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Through process improvement and advanced engineering, Westlake Plastics introduces the next generation of heat-stabilized polypropylene. Propylux 290 is produced from a FDA approved homopolymer resin, and exhibits better heat and dimensional stability over Propylux.Applications Include:Tanks/tank coversFood strainersHot fillersWelding cabinetryEtching rinse tubsGlove BoxesCutting boardFan shroud and bladesAdvantages of Propylux 290:Excellent chemical resistanceLot controlled and traceableLow moisture absorptionFDA resinSuperior dimensional stabilityInformation provided by Westlake Plastics Company.

Physical Properties	Metric	English	Comments
Specific Gravity	0.920 g/cc	0.920 g/cc	ASTM D792
Water Absorption	0.010 % @Time 86400 sec	0.010 % @Time 24.0 hour	ASTM D570

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	100	100	ASTM D785
Tensile Strength at Break	29.2 MPa	4230 psi	ASTM D638
Tensile Strength, Yield	34.3 MPa	4970 psi	ASTM D638
Elongation at Break	70 %	70 %	ASTM D638
Elongation at Yield	5.0 %	5.0 %	ASTM D638
Tensile Modulus	2.20 GPa	319 ksi	ASTM D638
Flexural Strength	64.6 MPa	9370 psi	ASTM D790
Flexural Modulus	2.27 GPa	329 ksi	ASTM D790
Compressive Yield Strength	47.4 MPa	6880 psi	ASTM D695
Izod Impact, Notched	1.60 J/cm	3.00 ft-lb/in	ASTM D256
Izod Impact, Unnotched	NB	NB	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear	78.7 µm/m-°C	43.7 µin/in-°F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	154 °C	309 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	93.9 °C	201 °F	ASTM D648
Flammability, UL94	HB	HB