Westlake Mxsten CV77523 Polyethylene Plastomer

Category	Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer	Westlake Chemical Corporation
Trade Name	Mxsten
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Westlake Mxsten CV77523 Polyethylene Plastomer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Mxsten CV plastomer CV77523 is a polyethylene plastomer designed for blown film extrusion that contains high slip, very high antiblock and polymer processing aid additives. Films produced with this resin exhibit very good strength properties and low seal initiation temperatures.Application/UsesAgricultural tubingBlown filmCo-ex filmsFDA: This material complies with FDA regulations in 21 CFR, section 177.1520.All information provided by Westlake Chemical

Physical Properties	Metric	English	Comments
Density	0.906 g/cc	0.0327 lb/in³	ASTM D1505
Thickness	25.4 microns	1.00 mil
Melt Flow	0.50 g/10 min	0.50 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, TD	7.58 MPa	1100 psi	ASTM D882
Film Elongation at Break, MD	600 %	600 %	ASTM D882
Film Elongation at Break, TD	1000 %	1000 %	ASTM D882
Elmendorf Tear Strength MD	450 g	450 g	ASTM D1922
Elmendorf Tear Strength TD	650 g	650 g	ASTM D1922
Dart Drop	47.2 g/micron	1200 g/mil	ASTM D1709
Film Tensile Strength at Break, MD	62.1 MPa	9000 psi	ASTM D882
Film Tensile Strength at Break, TD	44.8 MPa	6500 psi	ASTM D882
1% Secant Modulus, MD	124 MPa	18000 psi	ASTM D882
1% Secant Modulus, TD	145 MPa	21000 psi	ASTM D882
Heat Seal Strength Initiation Temperature	82.0 °C	180 °F	Westlake

Optical Properties	Metric	English	Comments
Haze	30 %	30 %	ASTM D1003
Gloss	35 %	35 %	at 45º; ASTM D2457

Processing Properties	Metric	English	Comments
Blow-up Ratio (BUR)	2.4	2.4

Descriptive Properties	Value	Comments
Process	Blown Film
	Film
Region	US & Canada	Bamberger Polymers Distribution