Axiall UV-7160 Rigid PVC, Molding

Category	Polymer , Thermoplastic , Vinyl (PVC)
Manufacturer	Axiall
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Axiall UV-7160 Rigid PVC, Molding.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Georgia Gulf UV-7160 is a rigid vinyl injection molding compound characterized by excellent flow, toughness, heat stability, color hold and surface appearance. This combination of outstanding attributes makes it an ideal material choice for Class A appearance parts such as monochrome computer monitor housings, computer keyboard enclosures and appliance parts.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.

Physical Properties	Metric	English	Comments
Specific Gravity	1.35 g/cc	1.35 g/cc	ASTM D-792
Linear Mold Shrinkage	0.0030 - 0.0040 cm/cm	0.0030 - 0.0040 in/in	ASTM D-955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	100	100	ASTM D-785
Tensile Strength, Yield	41.4 MPa	6000 psi	ASTM D-638
Tensile Modulus	2.41 GPa	350 ksi	ASTM D-638
Flexural Strength	75.8 MPa	11000 psi	ASTM D-790
Flexural Modulus	2.59 GPa	375 ksi	ASTM D-790
Izod Impact, Notched	0.534 J/cm @Thickness 3.17 mm, Temperature -20.0 °C	1.00 ft-lb/in @Thickness 0.125 in, Temperature -4.00 °F	ASTM D-256
	7.47 J/cm @Thickness 3.17 mm, Temperature 23.0 °C	14.0 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	ASTM D-256
Gardner Impact	25.3 J @Temperature 23.0 °C	18.7 ft-lb @Temperature 73.4 °F	1/2" R Tup, 62 mil

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	70.0 °C	158 °F	ASTM D-648
Deflection Temperature at 1.8 MPa (264 psi)	74.00 °C	165.2 °F	ASTM D-648
Flammability, UL94	5VA	5VA
Flame Spread Index	50	50	RP; ASTM E-162
Oxygen Index	36 %	36 %	ASTM D-2863

Descriptive Properties	Value	Comments
Flow Ratio (Distance/Wall Thickness, 390-400°F)	215	Georgia Gulf Test
UL Weatherability Rating	F(1)	UL-746C