- Victrex® PEEK 450GL15 Polyetheretherketone, 15% Glass Fibre Reinforced
Victrex® PEEK 450GL15 Polyetheretherketone, 15% Glass Fibre Reinforced
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Glass Fiber Filled |
| Manufacturer | Victrex |
| Trade Name | PEEK |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Victrex® PEEK 450GL15 Polyetheretherketone, 15% Glass Fibre Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description:High performance thermoplastic material, 15% glass fibre reinforced Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding and extrusion, standard flow, FDA food contact compliant, colour natural/beige.Typical Application Areas:Applications for higher strength in a static system. Low coefficient of thermal expansion. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications.Information Provided by VICTREX®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | Crystalline; ISO 1183 |
| Water Absorption at Saturation | 0.40 % @Temperature 23.0 °C |
0.40 % @Temperature 73.4 °F |
Equilibrium; by immersion; ISO 62-1 |
| 0.50 % @Temperature 100 °C |
0.50 % @Temperature 212 °F |
immersion; ISO 62-1 | |
| Viscosity | 450000 cP @Temperature 400 °C |
450000 cP @Temperature 752 °F |
melt; ISO 11443 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | 360°C nozzle, 160°C tool; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | 380°C nozzle, 180°C tool; ISO 294-4 |
| Spiral Flow | 10.0 cm @Thickness 1.00 mm |
3.94 in @Thickness 0.0394 in |
380°C nozzle, 180°C tool |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 96 @Temperature 23.0 °C |
96 @Temperature 73.4 °F |
ISO 868 |
| Tensile Strength at Break | 25.0 MPa @Temperature 275 °C |
3630 psi @Temperature 527 °F |
ISO 527 |
| 45.0 MPa @Temperature 175 °C |
6530 psi @Temperature 347 °F |
ISO 527 | |
| 80.0 MPa @Temperature 125 °C |
11600 psi @Temperature 257 °F |
ISO 527 | |
| 140 MPa @Temperature 23.0 °C |
20300 psi @Temperature 73.4 °F |
ISO 527 | |
| Elongation at Break | 4.0 % @Temperature 23.0 °C |
4.0 % @Temperature 73.4 °F |
ISO 527 |
| Tensile Modulus | 7.50 GPa @Temperature 23.0 °C |
1090 ksi @Temperature 73.4 °F |
ISO 527 |
| Flexural Strength | 240 MPa @Temperature 23.0 °C |
34800 psi @Temperature 73.4 °F |
ISO 178 |
| Flexural Modulus | 7.20 GPa @Temperature 23.0 °C |
1040 ksi @Temperature 73.4 °F |
ISO 178 |
| Compressive Strength | 40.0 MPa @Temperature 200 °C |
5800 psi @Temperature 392 °F |
ISO 604 |
| 130 MPa @Temperature 120 °C |
18900 psi @Temperature 248 °F |
ISO 604 | |
| 200 MPa @Temperature 23.0 °C |
29000 psi @Temperature 73.4 °F |
ISO 604 | |
| Izod Impact, Notched (ISO) | 0.700 kJ/m² @Temperature 23.0 °C |
0.333 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A |
| Izod Impact, Unnotched (ISO) | 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
ISO 180/U |
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1U |
| Charpy Impact, Notched | 0.550 J/cm² @Temperature 23.0 °C |
2.62 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 50.0 µm/m-°C @Temperature <=143 °C |
27.8 µin/in-°F @Temperature <=289 °F |
Average below Tg; ISO 11359 |
| 125 µm/m-°C @Temperature >=143 °C |
69.4 µin/in-°F @Temperature >=289 °F |
Average above Tg; ISO 11359 | |
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C @Temperature <=143 °C |
13.9 µin/in-°F @Temperature <=289 °F |
Below Tg; ISO 11359 |
| 30.0 µm/m-°C @Temperature >=143 °C |
16.7 µin/in-°F @Temperature >=289 °F |
Above Tg; ISO 11359 | |
| Thermal Conductivity | 0.350 W/m-K | 2.43 BTU-in/hr-ft²-°F | Along flow; ISO 22007-4 |
| 0.300 W/m-K @Temperature 23.0 °C |
2.08 BTU-in/hr-ft²-°F @Temperature 73.4 °F |
Average; ISO/CD 22007-4 | |
| Melting Point | 343 °C | 649 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 298 °C | 568 °F | ISO 75-f |
| Glass Transition Temp, Tg | 143 °C | 289 °F | Onset; ISO 11357 |
| 150 °C | 302 °F | Midpoint; ISO 11357 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.1 @Frequency 1000 Hz, Temperature 23.0 °C |
3.1 @Frequency 1000 Hz, Temperature 73.4 °F |
IEC 60250 |
| Dielectric Strength | 24.0 kV/mm @Thickness 5.00 mm |
610 kV/in @Thickness 0.197 in |
IEC 60243-1 |
| Dissipation Factor | 0.0050 @Frequency 1.00e+6 Hz, Temperature 23.0 °C |
0.0050 @Frequency 1.00e+6 Hz, Temperature 73.4 °F |
IEC 60250 |
| Comparative Tracking Index | 150 V | 150 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 100 °C | <= 212 °F | Hopper Temperature |
| Nozzle Temperature | 380 °C | 716 °F | |
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |
| Drying Temperature | 120 °C @Time 18000 sec |
248 °F @Time 5.00 hour |
|
| 150 °C @Time 10800 sec |
302 °F @Time 3.00 hour |
Users viewing this material also viewed the following:
- DuPont Performance Polymers Zytel® 70G30HSL BK039B Nylon 66 (Unverified Data**)
- LG Chemical LUPOS GP2206F ABS+GF20%, Flame Retardant
- DuPont Elvax® 3182-2 Ethylene Vinyl Acetate
- Loctite® Output™ 315 Acrylic Adhesive
- Fainplast Compounds FR 89 Flexible PVC, Insulation
- Aclo Accutech Polypropylene Homopolymer HP0334C30L1 Calcium Reinforced
- Aaron Industries AAROPRENE® ATPR 1000 60A Elastomeric Compound
- Asahi Kasei Xyron® 100Z Modified Polyphenylene Ether
Copyright © lookpolymers.com All Rights Reserved