Victrex® APTIV® 2102-100M Polyetheretherketone (PEEK) Polymer Film, Amorphous, Mineral Filled

Category	Polymer , Film , Thermoplastic , Polyketone , Polyetheretherketone (PEEK)
Manufacturer	Victrex
Trade Name	APTIV®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Victrex® APTIV® 2102-100M Polyetheretherketone (PEEK) Polymer Film, Amorphous, Mineral Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

APTIV® 2100 series films are the mineral filled amorphous films made from VICTREX® PEEK polymer. The film provides a material solution for engineers in ultra-high performance applications. APTIV films are a comprehensive range of versatile, high-performance films, the use of which can facilitate reduced systems costs, improved performance and enhanced design freedom. APTIV 2100 has a unique combination of properties providing high temperature performance, lightweight, mechanical strength, durability, excellent radiation, hydrolysis and chemical resistance, electrical insulation, excellent barrier properties with high purity, good flammability without the use of flame retardants, low toxicity of combustion products, and low moisture absorption in a film format. Inherently halogen-free and ease of processing makes APTIV films a technology enabler for our customers and end users. APTIV 2100 series provides a higher modulus over the APTIV 2000 series amorphous films. This grade is tailored towards thermoforming of thin wall parts with higher modulus, such as speaker diaphragms.Applications Electrical insulation Acoustic speaker diaphragms Thermoforming of thin wall partsProperties measured on 50 micron film

Physical Properties	Metric	English	Comments
Specific Gravity	1.42 g/cc @Temperature 23.0 °C	1.42 g/cc @Temperature 73.4 °F	ISO 1183

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	>= 150 % @Thickness 0.100 mm	>= 150 % @Thickness 0.00394 in	ISO 527
	>= 150 % @Thickness 0.100 mm	>= 150 % @Thickness 0.00394 in	ISO 527
Film Elongation at Break, TD	>= 150 % @Thickness 0.125 mm	>= 150 % @Thickness 0.00492 in	ISO 527
	>= 150 % @Thickness 0.125 mm	>= 150 % @Thickness 0.00492 in	ISO 527
Tensile Modulus	3.00 GPa @Thickness 0.100 mm	435 ksi @Thickness 0.00394 in	TD; ISO 527
	3.00 GPa @Thickness 0.125 mm	435 ksi @Thickness 0.00492 in	MD; ISO 527
	3.00 GPa @Thickness 0.125 mm	435 ksi @Thickness 0.00492 in	TD; ISO 527
	3.50 GPa @Thickness 0.100 mm	508 ksi @Thickness 0.00394 in	MD; ISO 527
Film Tensile Strength at Break, MD	90.0 MPa @Thickness 0.100 mm	13100 psi @Thickness 0.00394 in	ISO 527
	100 MPa @Thickness 0.100 mm	14500 psi @Thickness 0.00394 in	ISO 527
Film Tensile Strength at Break, TD	80.0 MPa @Thickness 0.125 mm	11600 psi @Thickness 0.00492 in	ISO 527
	100 MPa @Thickness 0.125 mm	14500 psi @Thickness 0.00492 in	ISO 527

Thermal Properties	Metric	English	Comments
Shrinkage, MD	<= 0.50 % @Thickness 0.100 mm	<= 0.50 % @Thickness 0.00394 in	TM-VX-84
Shrinkage, TD	<= 0.50 % @Thickness 1.00 mm	<= 0.50 % @Thickness 0.0394 in	TM-VX-84

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+16 ohm-cm @Temperature 23.0 °C	1.00e+16 ohm-cm @Temperature 73.4 °F	100V; ASTM D257