Unitika AX-1500 Conditioned

Category Polymer , Thermoplastic , Polyarylate
Manufacturer Unitika
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Unitika AX-1500 Conditioned.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AX series resins are opaque polymer alloys with a high deflection temperature under load without reinforcement and a chemical resistance as high as those of crystalline resins. They are excellent in moldability and provide molded products fewer in the number of sink marks, warps, and runoffs.Characteristics:Nonreinforced heat resistance: Deflection temperature under load without reinforcement: 1.8 MPa at 150°C Chemical resistance: As high as those of polyamide resins, except alkali resistance Adhesiveness: Chemical resistance and adhesiveness as high as those of crystalline resinsLubrication: As high as those of polyamide resins Molding accuracy: Fewer in the number of sink marks and warps, and lower (less than 1/3) in water absorption than polyamide resinsInformation provided by Unitika Ltd.
Mechanical Properties Metric English Comments
Tensile Strength at Break 53.0 MPa
7690 psi
ASTM D638
Elongation at Break 70 %
70 %
ASTM D638
Flexural Strength 76.0 MPa
11000 psi
ASTM D790
Flexural Modulus 1.20 GPa
174 ksi
ASTM D790
Izod Impact, Notched 1.96 J/cm

@Thickness 3.17 mm
3.67 ft-lb/in

@Thickness 0.125 in
ASTM D256
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
ASTM D257
Dielectric Constant 3.6

@Frequency 1.00e+6 Hz
3.6

@Frequency 1.00e+6 Hz
ASTM D150
Dielectric Strength 25.0 kV/mm
635 kV/in
ASTM D149
Dissipation Factor 0.040

@Frequency 1.00e+6 Hz
0.040

@Frequency 1.00e+6 Hz
ASTM D150
Comparative Tracking Index >= 600 V
>= 600 V
Processing Properties Metric English Comments
Rear Barrel Temperature 210 - 230 °C
410 - 446 °F
Middle Barrel Temperature 240 - 260 °C
464 - 500 °F
Front Barrel Temperature 250 - 270 °C
482 - 518 °F
Nozzle Temperature 250 - 270 °C
482 - 518 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
actual surface temp
Drying Temperature 100 °C
212 °F
Dry Time 10.0 - 24.0 hour
10.0 - 24.0 hour
Back Pressure 0.490 - 1.47 MPa
71.1 - 213 psi
gage pressure