UBE UBEPOL BR13HB HIPS (n-DM = 0.03 wt % and PH-3H = 0.03 wt %)

Category	Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified
Manufacturer	UBE
Trade Name	UBEPOL
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	UBE UBEPOL BR13HB HIPS (n-DM = 0.03 wt % and PH-3H = 0.03 wt %).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: UBEPOL-BR13HB is characterized by its low solution viscosity compared with conventional grades and short dissolution time in styrene monomer. Its main merits are as follows:Short dissolution time in styrene monomerSmall power consumption for agitation necessary for polymerization in HIPS manufacturing process High rubber content because of low solution viscosity gives HIPS of a higher impact strength It is easy to make rubber particle small in HIPS Information provided by UBE.

Physical Properties	Metric	English	Comments
Particle Size	0.80 µm	0.80 µm	Rubber Particle Size
Melt Flow	2.8 g/10 min	2.8 g/10 min

Mechanical Properties	Metric	English
Tensile Strength at Break	31.0 MPa	4500 psi
Tensile Strength, Yield	35.0 MPa	5080 psi
Elongation at Break	7.0 %	7.0 %
Izod Impact, Notched	0.530 J/cm	0.993 ft-lb/in

Thermal Properties	Metric	English	Comments
Vicat Softening Point	101 °C	214 °F

Optical Properties	Metric	English	Comments
Gloss	82 %	82 %

Descriptive Properties	Value	Comments
MEK/Acetone Insolubles (wt.%)	21.9
Swelling Index	13.7