Lanxess Pocan® DP 2004 000000 PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Flame Retardant , Polybutylene Terephthalate (PBT), Unreinforced, Molded |
| Manufacturer | Lanxess |
| Trade Name | Pocan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Pocan® DP 2004 000000 PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT, non-reinforced, injection molding, halogen free flame retardant
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0023 cm/cm | 0.0023 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0023 cm/cm | 0.0023 in/in | ISO 294-4, 2577 |
| Melt Flow | 82 g/10 min @Load 2.16 kg, Temperature 250 °C |
82 g/10 min @Load 4.76 lb, Temperature 482 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 53.0 MPa | 7690 psi | ISO 527-1/-2 |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ISO 527-1/-2 |
| Elongation at Break | 20 % | 20 % | ISO 527-1/-2 |
| Elongation at Yield | 8.0 % | 8.0 % | ISO 527-1/-2 |
| Tensile Modulus | 2.30 GPa | 334 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 8.50 J/cm² @Temperature 23.0 °C |
40.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 120 µm/m-°C | 66.7 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 120 µm/m-°C | 66.7 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 224 °C | 435 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 163 °C | 325 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C | 171 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 48.0 °C | 118 °F | ISO 75-1/-2 |
| Flammability, UL94 | V-2 @Thickness 0.750 mm |
V-2 @Thickness 0.0295 in |
IEC 60695-11-10 |
| V-2 @Thickness 1.50 mm |
V-2 @Thickness 0.0591 in |
IEC 60695-11-10 | |
| Oxygen Index | 28 % | 28 % | ISO 4589-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243-1 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 °C | 500 °F | Injection Molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Flame retarding agent | |
| Features | Flame retardant | |
| Form | Pellets | |
| ISO Shortname | ISO 7792-1-PBT,GFHMR,09-020; ISO 1043-PBT FR(30+40) | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Omni Plastics OmniTuff™ HPP GRC40 Homopolymer Polypropylene Glass Reinforced
- Polimeri Europa EDISTIR N1841 Polystyrene (discontinued **)
- LNP ULTEM® UC3000 Polyetherimide, 30% Carbon Fiber Reinforcement (discontinued **)
- Lehmann & Voss LUVOCOM® 1105-7568/GY PEEK, with PTFE
- SABIC Innovative Plastics LNP LUBRICOMP MX91206 PP
- Master Bond UV10TK Dimensionally Stable One Component UV Curable Adhesive
- A. Schulman POLYBATCH™ Orange LL10257/4 Concentrate Based In LLDPE
- Adell AT-14 Nylon 66, 20% Glass Reinforced; Impact Modified
- Arlon Thermabond® T-20 NP (99770W008) 0.008" (0.203 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier
Copyright © lookpolymers.com All Rights Reserved