Toyobo VYLOPET® CA5310 PC/PBT Polymer Alloy, High Rigidity, Impact Resistant
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Toyobo |
| Trade Name | VYLOPET® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo VYLOPET® CA5310 PC/PBT Polymer Alloy, High Rigidity, Impact Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Lamp partsHome electric appliance partsFeatures: Fine appearanceHigh rigidityImpact resistantInformation provided by Toyobo.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | 24 hrs at 23°C; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Thickness 3.00 mm |
0.0050 in/in @Thickness 0.118 in |
MD |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Thickness 3.00 mm |
0.0060 in/in @Thickness 0.118 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 87.0 MPa | 12600 psi | ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Strength | 136 MPa | 19700 psi | ASTM D790 |
| Flexural Modulus | 4.00 GPa | 580 ksi | ASTM D790 |
| Izod Impact, Notched | 0.520 J/cm | 0.974 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 128 °C | 262 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 270 °C | 518 °F | Molding temperature |
| Mold Temperature | 70.0 °C | 158 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 3 hour | 3 hour |
Users viewing this material also viewed the following:
- Hong Kun Group AO 3114 Antioxidant
- Techmer ES HiFill® HIPS 484 GY
- Saint-Gobain Tygon® S3™ Silver Antimicrobial Tubing
- Hexcel® Redux® 308A-NA Modified epoxy film adhesive
- ChevronTexaco Delo® 400 Synthetic, SAE 5W-40
- ExxonMobil LLDPE LL 3201.36 Linear Low Density Polyethylene Resin
- Arlon 910-05RXX-P0 0.010" (0.254 mm) Self-Fusing Silicone Tape
- DuPont Performance Polymers Neoprene 671A Polychloroprene (discontinued **)
- SABIC Innovative Plastics Xenoy® X5630 PC+PET (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved