Fujipoly Industries Sarcon® GR-n Gap Filler Pad

Category Polymer , Thermoset , Silicone
Manufacturer Fujipoly Industries
Trade Name Sarcon®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Fujipoly Industries Sarcon® GR-n Gap Filler Pad.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Sarcon GR-n is a highly formable, thermally conductive gel material (no electicity conductive) in a versatile sheet form that easily fits and adheres to most all shapes and sizes of components, and make reliable and complete physical contact. GR-Hn has a hardened top surfaceInformation provided by Fujipoly Industries
Physical Properties Metric English Comments
Specific Gravity 3.20 g/cc
3.20 g/cc
60°C for 1,000 hrs with 90% RH; JIS-K-6220
3.20 g/cc
3.20 g/cc
70°C for 1,000 hrs; JIS-K-6220
3.20 g/cc
3.20 g/cc
120°C for 1,000 hrs; JIS-K-6220
3.20 g/cc
3.20 g/cc
JIS-K-6220; ASTM D-792
3.20 g/cc
3.20 g/cc
150°C for 1,000 hrs with 90% RH; JIS-K-6220
Mechanical Properties Metric English Comments
Hardness, Shore C 50
50
SRIS0101
63
63
150°C for 1,000 hrs with 90% RH; SRIS0101
63
63
60°C for 1,000 hrs with 90% RH; SRIS0101
65
65
70°C for 1,000 hrs; SRIS0101
90
90
150°C for 1,000 hrs; SRIS0101
Hardness, Shore OO 64
64
ASTM D2240
Tensile Strength, Yield 0.200 MPa
29.0 psi
120°C for 1,000 hrs; JIS-K-6251(#2)
0.300 MPa
43.5 psi
JIS-K-6251(#2)/ASTM D-412
0.300 MPa
43.5 psi
70°C for 1,000 hrs; JIS-K-6251(#2)
0.400 MPa
58.0 psi
150°C for 1,000 hrs with 90% RH; JIS-K-6251(#2)
0.400 MPa
58.0 psi
60°C for 1,000 hrs with 90% RH; JIS-K-6251(#2)
Elongation at Yield 5.0 %
5.0 %
120°C for 1,000 hrs; JIS-K-6251(#2)
25 %
25 %
JIS-K-6251(#2)/ASTM D-412
25 %
25 %
70°C for 1,000 hrs; JIS-K-6251(#2)
75 %
75 %
150°C for 1,000 hrs with 90% RH; JIS-K-6251(#2)
75 %
75 %
60°C for 1,000 hrs with 90% RH; JIS-K-6251(#2)
Tear Strength 1.00 kN/m
5.71 pli
60°C for 1,000 hrs with 90% RH; JIS-K-6252
1.00 kN/m
5.71 pli
150°C for 1,000 hrs with 90% RH; JIS-K-6252 (Angle)
1.00 kN/m
5.71 pli
120°C for 1,000 hrs; JIS-K-6252 (Angle)
1.00 kN/m
5.71 pli
70°C for 1,000 hrs; JIS-K-6252 (Angle)
1.00 kN/m
5.71 pli
JIS-K-6252 (Angle)/ASTM D-624
Thermal Properties Metric English Comments
Thermal Conductivity 7.90 W/m-K
54.8 BTU-in/hr-ft²-°F
JIS-R-2618; ASTM D2326
7.90 W/m-K
54.8 BTU-in/hr-ft²-°F
120°C for 1,000 hrs; JIS-R-2618
7.90 W/m-K
54.8 BTU-in/hr-ft²-°F
150°C for 1,000 hrs with 90% RH; JIS-R-2618
7.90 W/m-K
54.8 BTU-in/hr-ft²-°F
60°C for 1,000 hrs with 90% RH; JIS-R-2618
7.90 W/m-K
54.8 BTU-in/hr-ft²-°F
70°C for 1,000 hrs; JIS-R-2618
Maximum Service Temperature, Air 200 °C
392 °F
Minimum Service Temperature, Air -60.0 °C
-76.0 °F
Electrical Properties Metric English Comments
Volume Resistivity 1.30e+11 ohm-cm
1.30e+11 ohm-cm
60°C for 1,000 hrs with 90% RH; JIS-K-6249
2.50e+11 ohm-cm
2.50e+11 ohm-cm
70°C for 1,000 hrs; JIS-K-6249
5.20e+12 ohm-cm
5.20e+12 ohm-cm
JIS-K-6249/ASTM D257
1.30e+14 ohm-cm
1.30e+14 ohm-cm
150°C for 1,000 hrs with 90% RH; JIS-K-6249
9.40e+14 ohm-cm
9.40e+14 ohm-cm
120°C for 1,000 hrs; JIS-K-6249
Dielectric Strength 18.0 kV/mm
457 kV/in
JIS-K-6249; ASTM D-149
18.0 kV/mm
457 kV/in
120°C for 1,000 hrs; JIS-K-6249
18.0 kV/mm
457 kV/in
150°C for 1,000 hrs with 90% RH; JIS-K-6249
18.0 kV/mm
457 kV/in
60°C for 1,000 hrs with 90% RH; JIS-K-6249
18.0 kV/mm
457 kV/in
70°C for 1,000 hrs; JIS-K-6249
Dielectric Breakdown 11000 V
11000 V
Withstand Voltage [V/min]; JIS-K-6249; ASTM D-149
Descriptive Properties Value Comments
Color Grey