Category | Polymer , Thermoplastic , Polypropylene (PP) |
Manufacturer | Total Atofina |
Trade Name | |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Total PPH 9020 Polypropylene, Homopolymer.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Bulk Density | 0.525 g/cc | 0.0190 lb/in³ | ISO 1183 |
Density | 0.905 g/cc | 0.0327 lb/in³ | ISO 1183 |
Melt Flow | 25 g/10 min @Load 2.16 kg, Temperature 230 °C |
25 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Hardness, Rockwell R | 98 | 98 | ISO 2039-2 |
Tensile Strength, Yield | 37.0 MPa | 5370 psi | ISO 527-2 |
Elongation at Yield | 8.0 % | 8.0 % | ISO 527-2 |
Tensile Modulus | 1.70 GPa | 247 ksi | ISO 527-2 |
Flexural Modulus | 1.60 GPa | 232 ksi | ISO 527-2 |
Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | ISO 179 |
Charpy Impact, Notched | 0.450 J/cm² | 2.14 ft-lb/in² | ISO 179 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Melting Point | 165 °C | 329 °F | ISO 3146 |
Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | 120°C per hour; ISO 75-2 |
Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | 120°C per hour; ISO 75-2 |
Vicat Softening Point | 90.0 °C | 194 °F | 50N-50°C per hour; ISO 306 |
153 °C | 307 °F | 10N-50°C per hour; ISO 306 |