Total PPC 4170 Polypropylene, Impact Copolymer, Blown Film Grade

Category Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer Total Atofina
Trade Name PPC
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total PPC 4170 Polypropylene, Impact Copolymer, Blown Film Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
TOTAL Petrochemicals Polypropylene 4170 is a polypropylene impact copolymer grade with good melt strength for use in the extrusion of blown films.Benefits. 4170 forms tough films with high dart impact strength, high heat resistance and excellent processability.FDA. 4170 complies with FDA regulations in paragraph (c) 3.2a of 21 CFR Section 177.1520 and may be used for articles or components of articles for contacting food during cooking. Recommended Applications. 4170 is recommended for use in blown film processes for the manufacture of heavy-duty bags, higher temperature requirement films, and matte finish labels. It can be used pure or in a variety of blended formulations for monolayer of co-extrusion applications.Information provided by Total Petrochemicals.
Physical Properties Metric English Comments
Specific Gravity 0.905 g/cc
0.905 g/cc
ASTM D1505
Water Vapor Transmission 6.98 g/m²/day

@Temperature 37.8 °C
0.450 g/100 in²/day

@Temperature 100 °F
100% RH; ASTM F1249
Oxygen Transmission Rate 2100 cc/m²/day

@Temperature 22.8 °C
135 cc/100 in²/day

@Temperature 73.0 °F
0% RH; ASTM D3985
Melt Flow 0.75 g/10 min

@Temperature 230 °C
0.75 g/10 min

@Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 26.2 MPa
3800 psi
ASTM D882
Film Tensile Strength at Yield, TD 24.8 MPa
3600 psi
ASTM D882
Film Elongation at Break, MD 750 %
750 %
ASTM D882
Film Elongation at Break, TD 770 %
770 %
ASTM D882
2% Secant Modulus 0.600 GPa
87.0 ksi
TD; ASTM D882
0.689 GPa
100 ksi
MD; ASTM D882
Elmendorf Tear Strength MD 55 g
55 g
ASTM D1922
Elmendorf Tear Strength TD 300 g
300 g
ASTM D1922
Dart Drop Test 350 g
0.772 lb
ASTM D1709, Method A
Film Tensile Strength at Break, MD 58.6 MPa
8500 psi
ASTM D882
Film Tensile Strength at Break, TD 37.9 MPa
5500 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 160 - 165 °C
320 - 329 °F
DSC
Optical Properties Metric English Comments
Haze 72 %
72 %
ASTM D1003
Gloss 7.0 %
7.0 %
at 45°; ASTM D2457
Processing Properties Metric English Comments
Melt Temperature 210 - 250 °C