Total PPC 11642 Polypropylene, Heterophasic Copolymer, Injection Molding

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded
Manufacturer	Total Atofina
Trade Name	PPC
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Total PPC 11642 Polypropylene, Heterophasic Copolymer, Injection Molding.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Polypropylene PPC 11642 is a nucleated antistatic heterophasic copolymer with high Melt Flow index of 60 g/10 min.Polypropylene PPC 11642 is characterized by high fluidity with good mechanical properties (balance of impact strength vs. stiffness). It has been formulated for excellent antistatic properties.Polypropylene PPC 11641 has been developed for high-speed injection molding of pails and thin wall food packaging.Peroxide is not used in the manufacturing of this product.Information provided by Total Petrochemicals.

Physical Properties	Metric	English	Comments
Specific Gravity	0.905 g/cc	0.905 g/cc	ISO 1183
Bulk Density	0.525 g/cc	0.0190 lb/in³	ISO 1183
Melt Flow	60 g/10 min @Load 2.16 kg, Temperature 230 °C	60 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	100	100	ISO 2039-2
Tensile Strength, Yield	27.0 MPa	3920 psi	ISO 527-2
Elongation at Yield	4.0 %	4.0 %	ISO 527-2
Tensile Modulus	1.60 GPa	232 ksi	ISO 527-2
Flexural Modulus	1.50 GPa	218 ksi	ISO 178
Izod Impact, Notched (ISO)	4.00 kJ/m² @Temperature -20.0 °C	1.90 ft-lb/in² @Temperature -4.00 °F	ISO 180
	7.00 kJ/m² @Temperature 23.0 °C	3.33 ft-lb/in² @Temperature 73.4 °F	ISO 180
Charpy Impact, Notched	0.450 J/cm² @Temperature -20.0 °C	2.14 ft-lb/in² @Temperature -4.00 °F	ISO 179
	0.650 J/cm² @Temperature 23.0 °C	3.09 ft-lb/in² @Temperature 73.4 °F	ISO 179

Thermal Properties	Metric	English	Comments
Melting Point	165 °C	329 °F	ISO 3146
Deflection Temperature at 0.46 MPa (66 psi)	112 °C	234 °F	120°C per hour; ISO 752
Deflection Temperature at 1.8 MPa (264 psi)	55.0 °C	131 °F	120°C per hour; ISO 752
Vicat Softening Point	80.0 °C @Load 5.10 kg	176 °F @Load 11.2 lb	50°C per hour; ISO 306
	148 °C @Load 1.02 kg	298 °F @Load 2.25 lb	50°C per hour; ISO 306