DuPont Performance Polymers Hypalon® 40 Chlorosulfonated Polyethylene Rubber, Peroxide Cured Carbon Black Filled Compound

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Rubber or Thermoset Elastomer (TSE) , Chlorosulfonated Polyethylene Rubber
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Hypalon® 40 Chlorosulfonated Polyethylene Rubber, Peroxide Cured Carbon Black Filled Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Carbon black compound with 100 parts Hypalon; 40 parts carbon black; 20 parts magnesia; and 5.8 parts Varox® DBPH-50. Physical property data below (except mooney viscosity) are for vulcanizate. MatWeb has other entries for different compounds of this Hypalon grade.General Hypalon® Information: Vulcanizates of this chlorosulfonated polyethylene synthetic rubber are highly resistant to ozone, oxygen, weather, heat, oil, and chemicals. Hypalon resists discoloration on exposure to light and is widely used in light-colored vulcanizates. It can be compounded to give excellent mechanical properties. Several grades are available, all of which may be processed and used in the usual manner for solid elastomeric vulcanizates. Various grades of Hypalon have been used in single-ply roofing systems; auto power steering and oil cooler hoses; chemical-resistant liners; cable sheathing; and other coatings.Information provided by DuPont Dow Elastomers.This former DuPont Dow Elastomers product line is now produced by DuPont Performance Elastomers.
Physical Properties Metric English Comments
Mooney Viscosity 50

@Temperature 135 °C
50

@Temperature 275 °F
ML 1+4.  Stock property.; ASTM D1646-81
Mechanical Properties Metric English Comments
Hardness, Shore A 76
76
ASTM D2240-81
Tensile Strength, Ultimate 19.1 MPa
2770 psi
ASTM D412-80
Elongation at Break 250 %
250 %
ASTM D412-80
100% Modulus 0.0158 GPa
2.29 ksi
ASTM D412-80
Compression Set 27 %

@Temperature 100 °C
27 %

@Temperature 212 °F
22 hr at 100°C. Method B. ASTM D395-69.