Total Lotrene® Q2018C Linear Low Density Polyethylene, Blown Film

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Butene, Film
Manufacturer Total Atofina
Trade Name Lotrene®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total Lotrene® Q2018C Linear Low Density Polyethylene, Blown Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Lotrene® Q2018 Series are Linear Low Density Polyethylene resins produced in a gas phase reactor using butene (C4) co-monomer. They are designed for film applications and can be used in pure form as well as blended with other PE resins, such as LDPE or HDPE and mPE resins for mono extrusion of co-extrusion process to modify film properties.Lotrene® Q2018 Series are suited for many applications in the field of consumer, industrial, food or hygiene packaging such as freezer film, bread bags, shoppers and bags as well as lamination film and multilayer packaging film.Lotrene® Q2018C is a cast film grade and contains thermal stabilizers.Information provided by Total Petrochemicals.
Physical Properties Metric English Comments
Specific Gravity 0.918 g/cc
0.918 g/cc
ISO 1183
Thickness 40.0 microns
1.57 mil
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Antiblock Level 0.000 ppm
0.000 ppm
Slip Level 0.000 ppm
0.000 ppm
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 11.0 MPa
1600 psi
ASTM D882
Film Tensile Strength at Yield, TD 11.0 MPa
1600 psi
ASTM D882
Film Elongation at Break, MD 850 %
850 %
ASTM D882
Film Elongation at Break, TD 900 %
900 %
ASTM D882
Elmendorf Tear Strength, MD 5.60 g/micron
142 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 10.7 g/micron
272 g/mil
ASTM D1922
Dart Drop Test 130 g
0.287 lb
F50; ASTM D1709
Film Tensile Strength at Break, MD 35.0 MPa
5080 psi
ASTM D882
Film Tensile Strength at Break, TD 32.0 MPa
4640 psi
ASTM D882
1% Secant Modulus, MD 215 MPa
31200 psi
ASTM D882
1% Secant Modulus, TD 245 MPa
35500 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 121 °C
250 °F
Crystalline; ISO 11357
Vicat Softening Point 100 °C
212 °F
ASTM D1525 (A120)
Optical Properties Metric English Comments
Haze 14 %
14 %
ASTM D1003
Gloss 55 %
55 %
at 45°; ASTM D2457
Processing Properties Metric English Comments
Processing Temperature 170 - 210 °C
338 - 410 °F
Extrusion
Melt Temperature 190 °C
374 °F
Die Opening >= 0.180 cm
>= 0.0709 in
Blow-up Ratio (BUR) 2.0 - 3.0
2.0 - 3.0