LTL Color Compounds ColorFast® PCT2018 PC/PBT Alloy
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | LTL Color Compounds |
| Trade Name | ColorFast® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LTL Color Compounds ColorFast® PCT2018 PC/PBT Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PC/PBT alloy with excellent low temperature impact strengthAll information provided by LTL Color Compounders, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Melt Flow | 10 g/10 min @Load 3.80 kg, Temperature 260 °C |
10 g/10 min @Load 8.38 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 38.6 MPa | 5600 psi | 2.0 in/min; ASTM D638 |
| Tensile Strength, Yield | 45.5 MPa | 6600 psi | 2.0 in/min; ASTM D638 |
| Elongation at Break | 140 % | 140 % | 2.0 in/min; ASTM D638 |
| Flexural Strength | 75.8 MPa | 11000 psi | 2.0 in/min; ASTM D790 |
| Flexural Modulus | 1.86 GPa | 270 ksi | 2.0 in/min; ASTM D790 |
| Izod Impact, Notched | 8.01 J/cm @Temperature 22.8 °C |
15.0 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
Users viewing this material also viewed the following:
- MV Labs RU490 [Ru(C10H8N2)3]Cl2·6H2O Tris(2,2'-bipyridyl)dichlororuthenium(II) dichloride hexahydrate
- Nylene® CX3451 Translucent Nylon Copolymer
- Solvay Specialty Polymers Amodel® ET-1001 L Polyphthalamide (PPA) Resin, Dry as Molded (discontinued **)
- Mallard Creek Polymers Rovene® 6016 Acrylic Emulsion
- Lord Adhesives 9010 Medium Viscosity, Odorless, Non-Frosting Methoxyethyl Cyanoacrylate Adhesive
- LyondellBasell Petrothene® LP510300 High Density Polyethylene, Film Extrusion Grade
- A. Schulman POLYFORT™ FPP 3443U UV Resistant Homopolymer Polypropylene
- A. Schulman POLYBLAK™ 3209 Superior Black Color Concentrate, 40% Carbon Black Based In Polypropylene
- DSM Akulon® K125 PA6
- Arlon 57226R020 0.020" (0.508 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved