Chosun Refractories PT-160 Plastic Refractory
| Category | Ceramic , Oxide , Silicon Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Chosun Refractories PT-160 Plastic Refractory.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 3.37e-7 - 0.000491 GPa <br>@Temperature 110 °C,<br> Time 86400 sec |
0.0000489 - 0.0711 ksi <br>@Temperature 230 °F,<br> Time 24.0 hour |
|
| 0.001962 - 0.004905 GPa <br>@Temperature 1350 °C,<br> Time 10800 sec |
0.2846 - 0.7114 ksi <br>@Temperature 2460 °F,<br> Time 3.00 hour |
||
| 0.004905 - 0.007848 GPa <br>@Temperature 1500 °C,<br> Time 10800 sec |
0.7114 - 1.138 ksi <br>@Temperature 2730 °F,<br> Time 3.00 hour |
||
| Compressive Strength | 2.94 - 7.85 MPa <br>@Temperature 110 °C,<br> Time 86400 sec |
427 - 1140 psi <br>@Temperature 230 °F,<br> Time 24.0 hour |
Cold Crushing Strength |
| 19.6 - 29.4 MPa <br>@Temperature 1350 °C,<br> Time 10800 sec |
2840 - 4270 psi <br>@Temperature 2460 °F,<br> Time 3.00 hour |
Cold Crushing Strength | |
| 24.5 - 34.3 MPa <br>@Temperature 1500 °C,<br> Time 10800 sec |
3560 - 4980 psi <br>@Temperature 2730 °F,<br> Time 3.00 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.97705 W/m-K <br>@Temperature 500 °C |
6.7697 BTU-in/hr-ft²-°F <br>@Temperature 932 °F |
|
| 1.0585 W/m-K <br>@Temperature 1000 °C |
7.3339 BTU-in/hr-ft²-°F <br>@Temperature 1830 °F |
||
| Maximum Service Temperature, Air | 1600 °C | 2910 °F | limited |
| Shrinkage | -0.700 % <br>@Temperature 110 °C,<br> Time 86400 sec |
-0.700 % <br>@Temperature 230 °F,<br> Time 24.0 hour |
|
| 0.00 % <br>@Temperature 1350 °C,<br> Time 10800 sec |
0.00 % <br>@Temperature 2460 °F,<br> Time 3.00 hour |
||
| 0.30 % <br>@Temperature 1500 °C,<br> Time 10800 sec |
0.30 % <br>@Temperature 2730 °F,<br> Time 3.00 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 41 % | 41 % | |
| SiO2 | 53 % | 53 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Main Applications | Volume Stability Spalling resistance | |
| Material Required for Estimating (kg/?) | 2,350 |
Users viewing this material also viewed the following:
- PolyOne Stat-Tech™ AS-10NCF/000 ABS - 10% Nickel Coated Carbon Fiber (discontinued **)
- Lubriplate SPO-222 Petroleum-Based Gear, Bearing, & Recirculating Oil
- Teknor Apex Fireguard® 910-NL1 Polyvinyl Chloride, Flexible
- Dow DS6D82 Polypropylene Resin
- Dynasol Calprene® H6170 Hydrogenated Rubber SEBS
- Cheng Yu Plastic IPS600UV Flame Retardant HIPS
- Polyplastics Duracon® M25-45 Acetal Co-polymer (POM), Weather resistance, High viscosity
- Haynes 556® alloy, 40% cold reduction, 1065°C anneal for 5 minutes
Copyright © lookpolymers.com All Rights Reserved