Total 2287 HDPE Bimodal Film Resin

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer	Total Atofina
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Total 2287 HDPE Bimodal Film Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Broad molecular weight distribution. Designed for die build-up sensitive equipmentApplications: T-shirt sacks, trash can liners, merchandise bags, deli wrapInformation provided provided by Total Petrochemicals.

Physical Properties	Metric	English	Comments
Density	0.951 g/cc	0.0344 lb/in³	ASTM D 792
Water Vapor Transmission	12.4 g/m²/day	0.799 g/100 in²/day	100°F; E 96/66
Thickness	20.3 microns	0.800 mil
Melt Flow	0.060 g/10 min @Load 2.16 kg	0.060 g/10 min @Load 4.76 lb	ASTM D 1238
	0.32 g/10 min @Load 5.00 kg	0.32 g/10 min @Load 11.0 lb	ASTM D 1238
High Load Melt Index	10 g/10 min @Load 21.6 kg	10 g/10 min @Load 47.6 lb	ASTM D 1238

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	>= 36.5 MPa	>= 5300 psi	ASTM D 882 A
Film Tensile Strength at Yield, TD	>= 34.5 MPa	>= 5000 psi	ASTM D 882 A
Film Elongation at Break, MD	300 - 500 %	300 - 500 %	ASTM D 882 A
Film Elongation at Break, TD	300 - 500 %	300 - 500 %	ASTM D 882 A
Secant Modulus, MD	0.841 GPa	122 ksi	ASTM D 882 A
Secant Modulus, TD	0.910 GPa	132 ksi	ASTM D 882 A
Elmendorf Tear Strength MD	24 g	24 g	ASTM D 1922
Elmendorf Tear Strength TD	120 g	120 g	ASTM D 1922
Dart Drop Test	350 g	0.772 lb	ASTM D 1709
Film Tensile Strength at Break, MD	>= 63.4 MPa	>= 9200 psi	ASTM D 882 A
Film Tensile Strength at Break, TD	>= 67.6 MPa	>= 9800 psi	ASTM D 882 A

Thermal Properties	Metric	English	Comments
Melting Point	127 °C	260 °F	ASTM D3417

Descriptive Properties	Value	Comments
Process	Film
Region	US & Canada	Bamberger Polymers Distribution