The NanoSteel® Company SHS 8000 TWAS Iron Based Alloy, Cored Wire
| Category | Metal , Ferrous Metal , Alloy Steel , Other Engineering Material , Ceramic/Metallic Coating |
| Manufacturer | The NanoSteel® Company |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | The NanoSteel® Company SHS 8000 TWAS Iron Based Alloy, Cored Wire.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Coating Description: SHS 8000 TWAS is a glass forming iron based alloy that forms a nanocomposite comprised of a mixed amorphous and nanoscale microstructure when sprayed as a coating. SHS 8000 features high wear resistance, elevated temperature erosion resistance and a unique high hardness/toughness combination.Key Performance CharacteristicsExcels in elevated temperature environments where fly ash and bed ash erosion occursSuperior bond strength without necessity of bond coatHardness increases as a function of time and temperatureApplication Process: Twin Wire Arc Spraying (TWAS)Information Provided by The NanoSteel Company, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.30 g/cc | 0.264 lb/in³ | Coating Property |
| Porosity | <= 5.0 % | <= 5.0 % | Coating Property |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Vickers Microhardness | 1064 - 1234 | 1064 - 1234 | kg/mm<sup>2</sup>; HV300 |
| >= 117 @Temperature 760 °C |
>= 117 @Temperature 1400 °F |
||
| >= 309 @Temperature 649 °C |
>= 309 @Temperature 1200 °F |
||
| >= 620 @Temperature 316 °C |
>= 620 @Temperature 600 °F |
||
| >= 912 @Temperature 149 °C |
>= 912 @Temperature 300 °F |
||
| >= 1030 @Temperature 21.1 °C |
>= 1030 @Temperature 70.0 °F |
||
| Adhesive Bond Strength | 78.6 MPa @Thickness 0.508 mm |
11400 psi @Thickness 0.0200 in |
1018 steel; ASTM C633-01 |
| Coefficient of Friction | 0.316 | 0.316 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 8.53 µm/m-°C @Temperature 100 - 500 °C |
4.74 µin/in-°F @Temperature 212 - 932 °F |
|
| Thermal Conductivity | 4.28 W/m-K @Temperature 23.0 °C |
29.7 BTU-in/hr-ft²-°F @Temperature 73.4 °F |
|
| 4.678 W/m-K @Temperature 50.0 °C |
32.47 BTU-in/hr-ft²-°F @Temperature 122 °F |
||
| 5.055 W/m-K @Temperature 75.0 °C |
35.08 BTU-in/hr-ft²-°F @Temperature 167 °F |
||
| 5.269 W/m-K @Temperature 100 °C |
36.57 BTU-in/hr-ft²-°F @Temperature 212 °F |
||
| 5.505 W/m-K @Temperature 125 °C |
38.20 BTU-in/hr-ft²-°F @Temperature 257 °F |
||
| 5.707 W/m-K @Temperature 150 °C |
39.61 BTU-in/hr-ft²-°F @Temperature 302 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Boron, B | <= 5.0 % | <= 5.0 % | |
| Carbon, C | <= 2.0 % | <= 2.0 % | |
| Chromium, Cr | <= 22 % | <= 22 % | |
| Iron, Fe | >= 59 % | >= 59 % | |
| Manganese, Mn | <= 1.0 % | <= 1.0 % | |
| Molybdenum, Mo | <= 5.0 % | <= 5.0 % | |
| Niobium, Nb (Columbium, Cb) | <= 5.0 % | <= 5.0 % | |
| Silicon, Si | <= 1.0 % | <= 1.0 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Impact Resistance | No delamination/cracking at 480 in-lbs | Drop Impact Testing |
| Wear Resistance Mass Loss (g) | 0.15 | 2000 cycles; ASTM G65-04 Procedure B |
Users viewing this material also viewed the following:
- Quadrant EPP Nylatron® GSM PA 6 + MoS2, cast (ISO Data)
- PTS Tristar® PC-10FR-(V18) 18 MFI Flame Retardant, UV Stabilized Polycarbonate With Release
- Arlon 920-410C##FR-P1 0.020" (0.508 mm) Cured Self-fusing Silicone Tape (discontinued **)
- A. Schulman POLYFORT™ FPP 3460 Glass-Mineral Hybrid Filled Copolymer
- Total PSI 3351 High Heat Resistance Impact Polystyrene
- EMS-Grivory Grivory® BGZ-50/2 PA6-I-GF50
- ExxonMobil Univis HVI 26
- Aclo Accuguard Polypropylene CP0467V2CSL Copolymer Flame Retardant Copper Stabilized
- Chase Plastics CP Pryme® N213GL (COND, 50% RH) Nylon 6, 13% Glass Fiber Reinforced, Internally Lubricated
Copyright © lookpolymers.com All Rights Reserved