Teknor Apex Uniprene® UN-1069A Thermoplastic Elastomer

Category	Polymer , Thermoplastic , Elastomer, TPE
Manufacturer	Teknor Apex Company
Trade Name	UNIPRENE®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Teknor Apex Uniprene® UN-1069A Thermoplastic Elastomer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Notes: Injection Rate: Fast Uses: Expansion Joint; Grommets; Tubing; Gaskets; Plugs; Weatherstripping; Glazing; Shock Absorbing Pads Forms: Pellets Processing Method: Extrusion; Injection Molding Extrusion Notes: Screw Speed: 30 to 100 rpmInformation Provided by Teknor Apex

Physical Properties	Metric	English	Comments
Specific Gravity	0.940 g/cc	0.940 g/cc	ASTM D792
Melt Flow	0.520 g/10 min @Load 5.00 kg, Temperature 230 °C	0.520 g/10 min @Load 11.0 lb, Temperature 446 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	74	74	5 seconds; ASTM D2240
	76	76	ASTM D2240
Tensile Strength at Break	9.24 MPa	1340 psi	ASTM D412
Tensile Stress	4.66 MPa @Strain 100 %	676 psi @Strain 100 %	ASTM D412
Elongation at Break	300 %	300 %	ASTM D412
Tear Strength	34.5 kN/m	197 pli	Die C; ASTM D624
Compression Set	50 % @Temperature 125 °C, Time 79200 sec	50 % @Temperature 257 °F, Time 22.0 hour	ASTM D395B

Processing Properties	Metric	English	Comments
Rear Barrel Temperature	173 - 213 °C	344 - 416 °F
Middle Barrel Temperature	179 - 219 °C	354 - 426 °F
Front Barrel Temperature	184 - 224 °C	364 - 436 °F
Nozzle Temperature	190 - 230 °C	374 - 446 °F
Zone 1	166 - 204 °C	330 - 400 °F
Zone 2	171 - 210 °C	340 - 410 °F
Zone 3	177 - 216 °C	350 - 420 °F
Zone 5	182 - 221 °C	360 - 430 °F
Die Temperature	190 - 227 °C	374 - 440 °F
Melt Temperature	190 - 230 °C	374 - 446 °F	Processing Temperature
Mold Temperature	35.0 - 60.0 °C	95.0 - 140 °F
Injection Pressure	1.38 - 6.89 MPa	200 - 1000 psi
Back Pressure	0.172 - 0.862 MPa	25.0 - 125 psi
Cushion	0.381 - 2.54 cm	0.150 - 1.00 in
Screw Speed	50 - 120 rpm	50 - 120 rpm

Descriptive Properties	Value	Comments
Appearance	Opaque