Teknor Apex TEKRON® 4300LM-P96-1 Thermoplastic Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber
Manufacturer Teknor Apex Company
Trade Name TEKRON®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Teknor Apex TEKRON® 4300LM-P96-1 Thermoplastic Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Teknor Apex Company
Physical Properties Metric English Comments
Specific Gravity 0.900 g/cc
0.900 g/cc
+/- 0.02; ASTM D792
Linear Mold Shrinkage, Flow 0.014 cm/cm
0.014 in/in
24 hours
0.016 cm/cm
0.016 in/in
24 hours + 30 min at 93°C
Linear Mold Shrinkage, Transverse 0.014 cm/cm
0.014 in/in
24 hours
0.016 cm/cm
0.016 in/in
24 hours + 30 min. at 93°C
Melt Flow 9.6 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 9.6 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 46
46
10 second delay. +/- 3; ASTM D2240
Tensile Strength, Yield 13.52 MPa
1961 psi
92% Retention; Air Over Aged 1000 hrs at 110°C
14.69 MPa
2131 psi
ASTM D412
Elongation at Break 19.402 %
19.402 %
89% Retention; Air Over Aged 1000 hrs at 110°C
21.8 %
21.8 %
ASTM D412
Flexural Modulus 0.31459 GPa
45.627 ksi
ASTM D790
Tear Strength 64.79 kN/m
369.6 pli
84% Retention, Air Over Aged 1000 hrs at 110°C
77.1 kN/m
440 pli
Die C; ASTM D1004
Thermal Properties Metric English Comments
CTE, linear 147 µm/m-°C

@Temperature 20.0 °C
 81.7 µin/in-°F

@Temperature 68.0 °F
CTE, linear, Transverse to Flow 132 µm/m-°C

@Temperature 20.0 °C
 73.3 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 58.0 °C
136 °F
Deflection Temperature at 1.8 MPa (264 psi) 39.0 °C
102 °F
Brittleness Temperature <= -65.0 °C
<= -85.0 °F
ASTM D746
Flame Spread 20.8 mm/min
0.820 in/min
Pass: Burn Rate- Max 100; FMVSS 302
Descriptive Properties Value Comments
Fogging 92, 3 hours at 100°C, cooling plate 21°C, value after 1 hour. (SAE-J1756)
92, 3 hours at 100°C, cooling plate 21°C, value after 16 hour. (SAE-J1756)