- Lanxess Pocan® B 1505 Z 000000 PBT
Lanxess Pocan® B 1505 Z 000000 PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Extrusion Grade , Polybutylene Terephthalate (PBT), Impact Grade , Polybutylene Terephthalate (PBT), Unreinforced, Molded |
| Manufacturer | Lanxess |
| Trade Name | Pocan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Pocan® B 1505 Z 000000 PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT, non-reinforced, injection molding, extrusion, impact modified
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ISO 1183 |
| Melt Flow | 26 g/10 min @Load 2.16 kg, Temperature 260 °C |
26 g/10 min @Load 4.76 lb, Temperature 500 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | ISO 527-1/-2 |
| Elongation at Break | 50 % | 50 % | Nominal; ISO 527-1/-2 |
| Elongation at Yield | 4.2 % | 4.2 % | ISO 527-1/-2 |
| Tensile Modulus | 2.40 GPa | 348 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 22.0 J/cm² @Temperature -30.0 °C |
105 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 105 µm/m-°C | 58.3 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 105 µm/m-°C | 58.3 µin/in-°F | ISO 11359-1/-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-1/-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 °C | 500 °F | Injection Molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Lubricants | |
| Release agent | ||
| Features | Heat stabilized or stable to heat | |
| High impact or high impact modified | ||
| Form | Pellets | |
| ISO Shortname | ISO 7792-1-PBT,GHMPR,11-020 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Noble Polymers Regis™ 155120 Thermoplastic Olefin (TPO)
- LyondellBasell Microthene® F FE53200 Ethylene Vinyl Acetate Copolymer
- Silikony Polskie Gumosil B Silicone Rubber
- CLAL-MSX NICLAL 1800 0 Annealed Copper Alloy, Free Cutting Nickel-Silver
- Ashley Polymers Ashlene® 527-43G Nylon 66, 43% Glass Reinforced
- Bhansali Engineering Santron IMS 2007LF SAN Resin
- 3M VHB™ F9469PC Adhesive Transfer Tapes with Adhesive 100MP
- Arkema Group KYNAR FLEX® 2850-07 Polyvinylidene Fluoride Copolymer - Extrusion & Molding
Copyright © lookpolymers.com All Rights Reserved