Teknor Apex Chemlon® 109 Nylon 66, Impact Grade
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade |
| Manufacturer | Teknor Apex Company |
| Trade Name | Chemlon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teknor Apex Chemlon® 109 Nylon 66, Impact Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Notes: High-Impact; Exceptional impact strength, especially at low temperatures; FMVSS Flammability: Passes, FMVSS 302 Processing Method: Injection Molding Forms: Pellets Automotive Specifications: Chrysler MS-DB41 CPN2456 Color: 100% Color Match; Ford ESA-M4D379-A; GM GMP.PA66.021Information Provided by Teknor Apex
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.019 - 0.025 cm/cm | 0.019 - 0.025 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 51.7 MPa | 7500 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Elongation at Yield | 4.5 % | 4.5 % | ASTM D638 |
| Flexural Strength | 48.3 MPa | 7000 psi | ASTM D790 |
| Flexural Modulus | 1.72 GPa | 250 ksi | ASTM D790 |
| Izod Impact, Notched | 2.40 J/cm @Temperature -40.0 °C |
4.50 ft-lb/in @Temperature -40.0 °F |
ASTM D256 |
| 9.61 J/cm @Temperature 22.8 °C |
18.0 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 257 °C | 495 °F | DSC |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.8 °C | 145 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness 0.749 mm |
HB @Thickness 0.0295 in |
|
| Oxygen Index | 21 % | 21 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | ASTM D257 |
| Dielectric Strength | 9.84 kV/mm @Thickness 3.00 mm |
250 kV/in @Thickness 0.118 in |
ASTM D149 |
| Comparative Tracking Index | 600 V | 600 V | UL 746 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 241 - 257 °C | 465 - 495 °F | |
| Middle Barrel Temperature | 257 - 271 °C | 495 - 520 °F | |
| Front Barrel Temperature | 263 - 279 °C | 505 - 535 °F | |
| Nozzle Temperature | 263 - 282 °C | 505 - 540 °F | |
| Melt Temperature | 263 - 282 °C | 505 - 540 °F | Processing Temperature |
| Drying Temperature | 79.4 °C | 175 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Suggested Moisture, max | 0.2 | |
| Suggested Regrind, max | 25 |
Users viewing this material also viewed the following:
- Polykemi AB SCANMID 6 B12^ F25 FR6 Nylon 6, Glass Fiber Reinforced, Flame Retardant
- Styron CALIBREâ„¢ 300EP 22 Polycarbonate, General Purpose
- Tra-Con Tra-Bond 813J01 Silicone Encapsulant
- Eurotec® Tecodur® PB70 GR15 BK EF PBT, 15% glass fiber reinforced, black, suitable for electrostatic powder coating, gas injection grade
- ConocoPhillips Hydroclear Diamond Class® 46 Turbine Oil
- Eastman Tenite Propionate 358A4000018 Clear, Trsp Cellulose Acetate Propionate
- Ashley Polymers Ashlene® P263WO PPO
- Fainplast Compounds Hax™ HF 213 Flame Retardant Polyolefin Cable Compound
- Sumitomo Bakelite North America FM 1132P Cellulose Reinforced Phenolic Novolac
- Master Bond Supreme 46HT-2ND2 Two Component, Non-Drip, Toughened, Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved