- Techmer ES Plaslube® J-1/20/TF/20 NAT PA66
Techmer ES Plaslube® J-1/20/TF/20 NAT PA66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled |
| Manufacturer | Techmer ES |
| Trade Name | Plaslube® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Plaslube® J-1/20/TF/20 NAT PA66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D792 |
| Water Absorption | 0.60 % | 0.60 % | 24 Hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength at Break | 131 MPa | 19000 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 197 MPa | 28500 psi | ASTM D790 |
| Flexural Modulus | 6.21 GPa | 900 ksi | ASTM D790 |
| Compressive Strength | 193 MPa | 28000 psi | ASTM D695 |
| Izod Impact, Notched | 0.908 J/cm | 1.70 ft-lb/in | ASTM D256 |
Users viewing this material also viewed the following:
- PTS BLACK PPE/Nylon Alloy 30% Glass Filled
- Phillips 66 COPYLENE® CH023NX Polypropylene, Homopolymer, Thermoforming
- Chevron Phillips Xtel® XE5300NA Polyphenylene Sulfide Alloy (discontinued **)
- Michelman® Resisto Coat™ 39AF Abrasion resistance coating
- Techmer ES HiFill FR® ABS GF30 FR 30% Glass Filled
- Shandong Rike Chemical HELIâ„¢ K-120N PVC Processing Aid Series (PA)
- A. Schulman FORMION™ FI 372 Ionomer
- Westlake Plastics Lennite® Ultra High Molecular Weight Polyethylene
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 2.5 PHR Varox DBPH-50 Peroxide
- Plastcom SLOVALEN PH 51 T 20 Polypropylene Homopolymer, 20% Mineral Filled
Copyright © lookpolymers.com All Rights Reserved