- Chosun Refractories INCT135S Light-Weight Castable
Chosun Refractories INCT135S Light-Weight Castable
| Category | Ceramic |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories INCT135S Light-Weight Castable.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 3.37e-7 - 0.00147 GPa @Temperature 110 °C, Time 86400 sec |
0.0000489 - 0.213 ksi @Temperature 230 °F, Time 24.0 hour |
|
| 0.0004905 - 0.0024525 GPa @Temperature 500 °C, Time 10800 sec |
0.07114 - 0.35571 ksi @Temperature 932 °F, Time 3.00 hour |
||
| 0.0014715 - 0.0044145 GPa @Temperature 1000 °C, Time 10800 sec |
0.21343 - 0.64028 ksi @Temperature 1830 °F, Time 3.00 hour |
||
| Compressive Strength | 2.94 - 7.85 MPa @Temperature 500 °C, Time 10800 sec |
427 - 1140 psi @Temperature 932 °F, Time 3.00 hour |
Cold Crushing Strength |
| 2.94 - 7.85 MPa @Temperature 1000 °C, Time 10800 sec |
427 - 1140 psi @Temperature 1830 °F, Time 3.00 hour |
Cold Crushing Strength | |
| 4.90 - 9.81 MPa @Temperature 110 °C, Time 86400 sec |
711 - 1420 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.291 W/m-K @Temperature 260 °C |
2.01 BTU-in/hr-ft²-°F @Temperature 500 °F |
|
| 0.3257 W/m-K @Temperature 540 °C |
2.257 BTU-in/hr-ft²-°F @Temperature 1000 °F |
||
| 0.3606 W/m-K @Temperature 800 °C |
2.498 BTU-in/hr-ft²-°F @Temperature 1470 °F |
||
| Maximum Service Temperature, Air | 1350 °C | 2460 °F | limited |
| Shrinkage | -0.400 % @Temperature 1000 °C, Time 10800 sec |
-0.400 % @Temperature 1830 °F, Time 3.00 hour |
|
| -0.0600 % @Temperature 110 °C, Time 86400 sec |
-0.0600 % @Temperature 230 °F, Time 24.0 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 43 % | 43 % | |
| SiO2 | 38 % | 38 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Casting, Troweling | |
| Main Applications | High temperature Low thermal conductivity | |
| Material Required for Estimating (kg/?) | 900 | |
| Water Required for Casting(%) | 45-55 |
Users viewing this material also viewed the following:
- MV Labs LU200 LuBr3·xH2O Lutetium bromide hydrate
- SABIC Innovative Plastics Cycoloy® CY5005 PC+ABS
- Polymer Resources TP-FRG15 Polybutylene Terephthalate, 15% Glass Reinforced, Flame Retardant
- Solvay Specialty Polymers AvaSpire® AV-755 SL45 Polyaryletherketone (PAEK) (Unverified Data**)
- PolyMirae Moplen HP500G Sheet and Thermoforming Grade Polypropylene
- PolyOne Geon™ Vinyl Flexible P484B Polyvinyl Chloride, Flexible (PVC, Flexible)
- Kingfa PC-S609 Toughened PC
- Solvay TECHNYL® R AR 130/GF Nylon 66, 30% glass fiber, DRY
- CoorsTek ADOS-90R 91% Alumina Thick Film Substrate
Copyright © lookpolymers.com All Rights Reserved