Techmer ES Luriblend® PA6/6 GF40 TL10 40% Glass Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled , Nylon 66, Heat Stabilized , Nylon 66, PTFE Filled |
| Manufacturer | Techmer ES |
| Trade Name | Luriblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Luriblend® PA6/6 GF40 TL10 40% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 40% Filler by WeightAdditive: Heat Stabilizer and PTFE Lubricant(10%)Features: Lubricated and Heat StabilizedInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in³ | ASTM D792 |
| Water Absorption | 0.60 % @Time 86400 sec |
0.60 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 3.17 mm |
0.0040 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength, Yield | 181 MPa | 26200 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 303 MPa | 44000 psi | ASTM D790 |
| Flexural Modulus | 10.3 GPa | 1500 ksi | ASTM D790 |
| Izod Impact, Notched | 1.44 J/cm @Thickness 3.17 mm |
2.70 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 12.8 J/cm @Thickness 3.17 mm |
24.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 19.8 µm/m-°C | 11.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 499 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Quadrant EPP Duratron® PAI T5530 Compression Molded Glass Reinforced Polyamide-imide (ASTM Product Data Sheet)
- FloMet 316L Stainless Steel
- Lehmann & Voss LUVOCOM® 1104-8327 Polyether ketone, with glass fiber, easy flowing
- Sax Polymers SAXALEN PPH305G30 Polypropylene Homopolymer, 30% Glass Filled
- A. Schulman SCHULAMID® 66 MK4015H 40% Glass Fiber/Mineral Reinforced, Heat Stabilized Nylon 66
- Eurostar Staramide BT6 PA6, 30% Mineral Filled, Injection Molded
- Dow Saran® 506 Polymer
- BASF N-Acetylmorpholine
- 3M Scotchcast™ 5230N Electrical Epoxy Powder Resin
- Fainplast Compounds PM 8020 Flexible PVC, Lead Free
Copyright © lookpolymers.com All Rights Reserved