Techmer ES HiFill® PPS 0231 B LE
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® PPS 0231 B LE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFeatures: High Density and Low ExtractablesAppearance: OpaqueInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.31 g/cc | 0.0835 lb/in³ | ASTM D792 |
| Water Absorption | 0.020 % @Time 86400 sec |
0.020 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 3.17 mm |
0.0030 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 100 | 100 | ASTM D785 |
| Tensile Strength, Yield | 131 MPa | 19000 psi | ASTM D638 |
| Elongation at Break | 1.1 % | 1.1 % | ASTM D638 |
| Flexural Strength | 179 MPa | 26000 psi | ASTM D790 |
| Flexural Modulus | 12.4 GPa | 1800 ksi | ASTM D790 |
| Izod Impact, Notched | 0.587 J/cm @Thickness 3.17 mm |
1.10 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 16.2 µm/m-°C | 9.00 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 280 °C | 536 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 266 °C | 510 °F | Unannealed; ASTM D648 |
| UL RTI, Electrical | 220 °C @Thickness 1.50 mm |
428 °F @Thickness 0.0591 in |
UL746 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 20.9 kV/mm | 530 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Nilit FRIANYL B63 SI20 Nylon 6 for injection molding
- Mallard Creek Polymers ROVENE® 4402 SBR Latex
- LG Chemical LUPOY SC2202 PC+GF20%, High Impact
- Michelman® Michem® Emulsion 45745P Nonionic Polyethylene wax emulsion
- Heatbath/Park Alu-Braze 960 Aluminum Brazing Salt
- SABIC Innovative Plastics LNP LUBRICOMP MX06404 PP (Asia Pacific)
- SABIC Innovative Plastics LNP Lubricomp LL003E PEEK
- Total HDPE 7195 High Density Polyethylene, Specialty Extrusion Resin
- Wellman Wellamid® MRB40K004-WT1 40% Mineral Reinforced Nylon 66
Copyright © lookpolymers.com All Rights Reserved