Techmer ES HiFill® POM CO 0167 S1 LE Acetal
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Steel Filled |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Techmer ES HiFill® POM CO 0167 S1 LE Acetal.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: MetalFeatures: Copolymer and Low ExtractablesInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in³ | ASTM D792 |
| Water Absorption | 0.20 % <br>@Time 86400 sec |
0.20 % <br>@Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.016 cm/cm <br>@Thickness 3.17 mm |
0.016 in/in <br>@Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 9.0 g/10 min <br>@Load 2.16 kg,<br> Temperature 190 °C |
9.0 g/10 min <br>@Load 4.76 lb,<br> Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 100 | 100 | ASTM D785 |
| Tensile Strength, Yield | 51.7 MPa | 7500 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Flexural Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 3.03 GPa | 440 ksi | ASTM D790 |
| Izod Impact, Notched | 0.587 J/cm <br>@Thickness 3.17 mm |
1.10 ft-lb/in <br>@Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 21.6 µm/m-°C | 12.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PC 13 T 30 PP, 30% mineral filling
- Polymer Resources PC-FR3-D-[color]-3 Polycarbonate, Improved Flame Retardant, High Flow, UV-stabilized
- Resin Technology Group Fusion 830 General Purpose Fusion Cyanoacrylate
- Isoflon PTFE + 3% MoS2 Polytetrafluoroethylene with 3% Molybdenum disulfide
- Indium Corp. 99.999% InI3 Indium Triiodide
- DuPont Bynel® 41E556 Anhydride-Modified LLDPE Adhesive Resin
- A. Schulman ComAlloy® E-16558 30% Glass Fiber Reinforced Nylon
- EMS-Grivory Grivory® HTV-4H1 nat PA6T/6I-GF40
- Diamond Polymers DIAMALOY ABSPC 750 HF ABS/PC Alloy, Non-Halogen, Flame Retardant
- Aclo Accutech Polypropylene Homopolymer HP0334T20L Talc Reinforced
Copyright © lookpolymers.com All Rights Reserved