Techmer ES HiFill® PA6/6 GB10 L 10% Glass Bead Filler
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Bead Filled |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® PA6/6 GB10 L 10% Glass Bead Filler.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Bead, 10% Filler by WeightAdditive: LubricantFeatures: LubricatedInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM D792 |
| Water Absorption | 0.90 % @Time 86400 sec |
0.90 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.018 cm/cm @Thickness 3.17 mm |
0.018 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength, Yield | 75.8 MPa | 11000 psi | ASTM D638 |
| Elongation at Break | 3.5 % | 3.5 % | ASTM D638 |
| Flexural Strength | 117 MPa | 17000 psi | ASTM D790 |
| Flexural Modulus | 2.76 GPa | 400 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm @Thickness 3.17 mm |
0.600 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 2.03 J/cm @Thickness 3.17 mm |
3.80 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 59.4 µm/m-°C | 33.0 µin/in-°F | ASTM D696 |
| Melting Point | 255 °C | 491 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C | 450 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 16.1 kV/mm | 410 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Polikim EFALON® K-25 PTFE, 25% Carbon Filled
- SABIC Innovative Plastics LNP LUBRICOMP AI0019 ABS (Europe-Africa-Middle East)
- Flint Hills P6G4Z-097 Impact Copolymer Polypropylene
- Lucite International Lucite® 4FI Glass Separation Resin
- A. Schulman POLYFORT™ FPP 1007X Extra High Flow, Talc Fortified Homopolymer Polypropylene
- A. Schulman POLYBATCH™ Blue LL40434 Concentrate Based In LLDPE
- Zeon Chemicals Quintone® D200 Aliphatic Hydrocarbon Resin
- Dow Corning MH-1109 Fluid
- Cytec (Conap) FR-1271 Conapoxy® Resin / Conacure® Hardener
Copyright © lookpolymers.com All Rights Reserved