- Techmer ES HiFill® PA6 GF/M30 HS BK 10/20% Glass/Mineral Filled
Techmer ES HiFill® PA6 GF/M30 HS BK 10/20% Glass/Mineral Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced , Nylon 6, Heat Stabilized |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® PA6 GF/M30 HS BK 10/20% Glass/Mineral Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 10% Filler by Weight and Mineral, 20% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Heat Stabilized and LubricatedAppearance: BlackTPCI# 7151102Information provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ASTM D792 |
| Water Absorption | 0.90 % @Time 86400 sec |
0.90 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.010 cm/cm @Thickness 3.17 mm |
0.010 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength, Yield | 75.8 MPa | 11000 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 |
| Flexural Modulus | 5.03 GPa | 730 ksi | ASTM D790 |
| Izod Impact, Notched | 0.187 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
0.350 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| 0.427 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
0.800 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.6 µm/m-°C | 17.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 196 °C | 385 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | ASTM D257 |
| Dielectric Strength | 15.7 kV/mm | 400 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Multibase Nylex™ 2185 HF Polyamide + PP
- Polimeri Europa Clearflex® FG 368 Octene Comonomer Linear Low Density Polyethylene
- NOVA Chemicals EPS M77B Expandable Polystyrene Resin
- LyondellBasell Petrothene® NA373244 Low Density Polyethylene, Cast/Blown Film Grade
- Mitsui UNISTOLEâ„¢ P-902M Polyolefinic Primer/ Adhesive
- Karina E 39/338-IE MBU Pink Color Concentrate
- Shin-Etsu Silicones KF-9007 Fluid
- Techmer ES Elastoblend® PA6/6 IM1 L 33% Glass Filled
- TPI Porene® ABS-GA800 High Impact ABS Resin
- 3M 4496W Double Coated Polyethylene Foam Tape
Copyright © lookpolymers.com All Rights Reserved