Techmer ES HiFill® HDPE TM40 40% Talc Filled
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® HDPE TM40 40% Talc Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Talc Filler, 40% Filler by WeightInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ASTM D792 |
| Water Absorption | 0.030 % @Time 86400 sec |
0.030 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.012 cm/cm @Thickness 3.17 mm |
0.012 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 70 | 70 | ASTM D785 |
| Tensile Strength, Yield | 32.8 MPa | 4750 psi | ASTM D638 |
| Elongation at Break | 9.0 % | 9.0 % | ASTM D638 |
| Flexural Strength | 51.7 MPa | 7500 psi | ASTM D790 |
| Flexural Modulus | 2.45 GPa | 355 ksi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm @Thickness 3.17 mm |
0.900 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 4.81 J/cm @Thickness 3.17 mm |
9.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 73.8 µm/m-°C | 41.0 µin/in-°F | ASTM D696 |
| Melting Point | 135 °C | 275 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 121 °C | 250 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.1 °C | 160 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 17.7 kV/mm | 450 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Polykemi AB SCANMID 6 B32^ EF F15 Nylon 6, Glass Fiber Reinforced, Modified
- Network Polymers NPS 80-0800 Crystal Polystyrene
- NOVA Chemicals Sclair® 14B3 Butene LMDPE Film Resin (discontinued **)
- Braskem PB 526 LDPE Blow Molding Polyethylene (discontinued **)
- LG Chemical Lupoy 1303-07 Polycarbonate Resin
- Shakespeare S-3 Economy Nylon Copolymer Fishing Line, 40 lb
- 3M FA021 Matte Clear Acetate Label Products
- Beijing Evergrow Resources PTFE Adhesive Tape
Copyright © lookpolymers.com All Rights Reserved