| Category | Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® ASA 814 GY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFeatures: Good Weather ResistanceAppearance: GrayInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 |
| Water Absorption | 0.35 % @Time 86400 sec |
0.35 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm @Thickness 3.17 mm |
0.0070 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 108 | 108 | ASTM D785 |
| Tensile Strength, Yield | 42.1 MPa | 6100 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 54.5 MPa | 7900 psi | ASTM D790 |
| Flexural Modulus | 1.86 GPa | 270 ksi | ASTM D790 |
| Izod Impact, Notched | 3.47 J/cm @Thickness 3.17 mm |
6.50 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 99.0 µm/m-°C | 55.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 88.9 °C | 192 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.2 °C | 171 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 5.00e+13 ohm-cm | 5.00e+13 ohm-cm | ASTM D257 |
| Dielectric Strength | 15.7 kV/mm | 400 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- PolyOne Lubri-Tech™ AT-000/5T Black Acetal-Copolymer, PTFE Lubricated (discontinued **)
- Lehmann & Voss LUVOCOM® 1700-8541 PPO, unreinforced
- Solvay Specialty Polymers Hylar® 5000 Polyvinylidene Fluoride (PVDF)
- Saint-Gobain CHR® M851 Polyester Film Backing Natural Rubber Adhesive Pressure Sensitive Tape
- A. Schulman FORMION™ FI 226 40% Glass Fiber Reinforced Ionomer / Nylon Alloy
- A. Schulman POLYBATCH™ Red 5670 Concentrate Based In Polyethylene
- Eastman Tenite 360E0096914 Cellulose Acetate Propionate, Natural, Trsp
- ExxonMobil Exxon™ 2211 Fast Cure Rate Grade
- Amity Thermosets ATS 166 Phenolic Molding Chopped cotton fabric Filler, Compression Molded
Copyright © lookpolymers.com All Rights Reserved